Processing and Characterization of Forged Poly(lactic acid)Screw
-
- KOBAYASHI Satoshi
- Graduate School of Science and Engineering, Tokyo Metropolitan University
Bibliographic Information
- Other Title
-
- 鍛造法によるポリ乳酸スクリューの成形とその評価
Abstract
Poly(lactic Acid) screws were fabricated using forging process. The process consisted of two-step, which included bar molding by drawing and threading. Molding temperatures were selected as 70 and 100℃. Machine-cut screws were also fabricated for comparison. In order to evaluate mechanical properties, pullout, shear and twists tests were conducted on the specimens. Higher pullout and shear strength were obtained for the screws forged at 70 ℃. Twist strength were almost the same values for screws molded at any conditions. However ductile behavior was observed for screws molded at 70℃. These results suggest that the forging at 70℃ is the best molding process.
Journal
-
- Materials System
-
Materials System 29 (0), 23-30, 2011
Materials System Research Laboratory, Kanazawa Institute of Technology
- Tweet
Details 詳細情報について
-
- CRID
- 1390287142242889216
-
- NII Article ID
- 130007987230
-
- ISSN
- 24359734
- 02866013
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- CiNii Articles
-
- Abstract License Flag
- Disallowed