High Strength Metallocene Catalyst-Synthesized Polypropylene Fibers with High Stereoregularity and High Molecular Weight
-
- Kunimitsu Tatsuma
- Faculty of Textile Science and Technology, Shinshu University
-
- Warashina Shuji
- Faculty of Textile Science and Technology, Shinshu University
-
- Ikaga Toshifumi
- Faculty of Textile Science and Technology, Shinshu University
-
- Kim KyoungHou
- Faculty of Textile Science and Technology, Shinshu University
-
- Ohkoshi Yutaka
- Faculty of Textile Science and Technology, Shinshu University Institute for Fiber Engineering, Shinshu University
-
- Koike Katsuhiko
- Prime Polymer Co., Ltd./Mitsui Chemicals Inc.,
抄録
<p>High stereoregularity isotactic polypropylene (iPP) can now be synthesized even using metallocene catalysts. Fibers with higher tensile strength than those of Ziegler-Natta catalyst-synthesized iPP have been reported for iPP with 20 g/10 min melt index. The aim of this study is to further increase the tensile strength using 4 g/10 min melt index iPP. Metallocene iPP fibers with higher tensile strength, higher initial modulus,and lower creep strain at 125 ̊C than Ziegler-Natta iPP fibers were also obtained using 4 g/10 min melt index iPP. Moreover, the obtained maximum tensile strength of 1.39 N/tex (1.3 GPa) was higher than that of 20 g/10 min melt index iPP. The metallocene iPP fibers also had smaller crack diameters estimated by ultra-small angle X-ray scattering.</p>
収録刊行物
-
- Journal of Fiber Science and Technology
-
Journal of Fiber Science and Technology 77 (2), 66-75, 2021-02-15
一般社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390568617215982464
-
- NII論文ID
- 130007990693
-
- ISSN
- 21897654
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可