Marginal discrepancy and load to fracture of monolithic zirconia laminate veneers: The effect of preparation design and sintering protocol
-
- SAKER Samah
- Fixed Prosthodontics Department, Faculty of Dentistry, Mansoura University
-
- ÖZCAN Mutlu
- Devision of Dental Biomaterials Unit, Center for Dental and Oral Medicine, Clinic for Reconstructive Dentistry
Search this article
Abstract
<p>To investigate and analyze the impact of teeth preparation designs and sintering protocol on marginal fit and fracture resistance of monolithic translucent zirconia laminate veneers. A total of 40 extracted intact human maxillary central incisors were assigned into 4 groups (n=10/each group) to investigate 2 variables: (1) the design of tooth preparation (a 1.5 mm incisal reduction with or without palatal chamfer) and (2) the two different sintering programs used for translucent zirconia restoration (standard or speed sintering procedure). Marginal discrepancy was evaluated using a digital microscope. The specimens were loaded to failure in the compression mode, using a universal testing machine with a crosshead speed of 0.5 mm/min. Marginal adaptation of monolithic translucent zirconia laminates are affected by both tooth preparation design and sintering protocol. However, resistance to fracture of translucent zirconia laminates has affected mainly by sintering procedure regardless the teeth preparation design used.</p>
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 40 (2), 331-338, 2021-03-25
The Japanese Society for Dental Materials and Devices