Microstructure and Mechanical Properties of the Heterogeneous-Nano Structured Cu–Be System Alloys
-
- Jiang H.
- Division of Mechanical Science and Engineering, Graduate School of Natural Science and Technology, Kanazawa University
-
- Watanabe C.
- Faculty of Mechanical Engineering, Institute of Natural Science and Engineering, Kanazawa University
-
- Miura H.
- Department of Mechanical Engineering, Toyohashi University of Technology
-
- Muramatsu N.
- Engineering and R&D, New Metals Division, NGK Insulators, Ltd.
この論文をさがす
抄録
<p>Microstructures and mechanical properties of Cu–Be–Co alloys having four different Be contents prepared by simply heavy cold rolling (CR) were systematically investigated. The cold-rolled alloys exhibited excellent mechanical properties due to development of heterogeneous nano-structure (HN), which consisted of “eye”-shape deformation twin domains surrounded by shear bands, and they were further embedded in conventional low-angle lamellae. The strength of each alloy increased with increasing Be content. The volume fraction of the twin domains quantitatively evaluated by the texture analyses that increased with increasing Be content rapidly from 0.40 mass% to 1.27 mass% and gradually from 1.27 mass% up to 2.14 mass%. The latter stagnation was attributed to the formation of coarse intermetallic particles, which impeded the formation of the HN structure. It revealed that the strength was correlated closely with the volume fraction of twin domains.</p><p> </p><p>This Paper was Originally Published in Japanese in J. Japan Institute of Copper 60 (2021) 81–86.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 63 (1), 21-26, 2022-01-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390572012411024256
-
- NII論文ID
- 130008134282
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 031899442
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可