SCM420浸炭鋼の高面圧下におけるすべりを伴う転がり疲労過程

• 橋本 和弥

  山陽特殊製鋼(株)研究・開発センター(現:同社自動車・産機営業部)

• 渕上 太一

  山陽特殊製鋼(株)研究・開発センター(現:同社技術企画管理部)

• 鑓 恵介

  UDトラックス(株)開発部門パワートレイン実験部

• 梅澤 修

  横浜国立大学大学院工学研究院

書誌事項

タイトル別名

• Rolling and Sliding Contact Fatigue Process under High Pressure in Carburized SCM420 Steel
• SCM420 シンタンコウ ノ コウメンアツ カ ニ オケル スベリ オ トモナウ コロガリ ヒロウ カテイ

抄録

It is important to improve fatigue life for pitting of gear in order to attempt down-sizing of gear unit and low fuel consumption. Rolling and sliding contact fatigue under high pressure in carburized SCM420 steel is studied. The ultimate aim is to understand the effect of material properties on the fatigue life. In this research, there was considerable interest in change of the material in the contact surface of specimens depending on the shift in tangential force acting on a moving roller in the direction of a tangent to the path of the roller during the fatigue test. Three lubricants were used in these fatigue tests for the purpose of changing the degree of tangential force. A roller tested under a lubricant that the tangential force is shifted higher compared with that of the other lubricant produced a pitting failure earlier. The roller also promoted to decrease the hardness and to narrow the half width of the (211) peak of alpha iron at the contact surface. The transition of these characteristics related to the creation of fine grain layer. That is regarded as worked structure formed during fatigue process. The depth of fine grain layer expands according to repeated loading. Fatigue crack propagation depth was almost equal to the depth of fine grain layer. Not only well-known softening caused by increase in temperature but also microstructural change caused by repeated stress loading have an effect on the life through the involvement in fatigue crack initiation and propagation behavior.

収録刊行物

• 鉄と鋼

  鉄と鋼 108 (1), 76-87, 2022

  一般社団法人 日本鉄鋼協会

キーワード

• rolling and sliding contact fatigue
• tangential force
• SCM420
• pitting
• microstructural change
• crack initiation and propagation

詳細情報

• CRID: 1390572045479390208
• NII論文ID: 130008138312
• NII書誌ID: AN00151251
• DOI: 10.2355/tetsutohagane.tetsu-2021-038
• ISSN: 18832954
• ISSN: 00211575
• NDL書誌ID: 031907984
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I031907984
• Web Site: https://www.jstage.jst.go.jp/article/tetsutohagane/108/1/108_TETSU-2021-038/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可