Growth and characterization of strontium-substituted La<sub>3</sub>Ta<sub>0.5</sub>Ga<sub>5.5</sub>O<sub>14</sub> single crystals
-
- TAKEDA Hiroaki
- Graduate School of Science and Engineering, Saitama University
-
- SOBATA Yudai
- Graduate School of Science and Engineering, Saitama University
-
- USUI Haruki
- School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- KODAMA Shohei
- Graduate School of Science and Engineering, Saitama University
-
- YANASE Ikuo
- Graduate School of Science and Engineering, Saitama University
-
- HOSHINA Takuya
- School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- TSURUMI Takaaki
- School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- SHIMAMURA Kiyoshi
- National Institute for Materials Science
抄録
<p>The effects of strontium substitution on the electrical properties of La3Ta0.5Ga5.5O14 (LTG) are reported. Strontium substituted LTG (Sr-LTG) with a nominal chemical composition La2.9Sr0.1Ta0.55Ga5.45O14 crystals were grown using the conventional Czochralski method under high and low oxygen partial pressures. The electrical properties and thermal behaviors of the Sr-LTG crystals were also compared with those of pure crystals. Sr substitution was found to affect the electroacoustic constants and thermal expansion coefficient clearly. These characteristics are discussed from crystallographic perspectives. The Sr-LTG crystals grown at low oxygen partial pressures exhibited higher electrical resistivity ρ for pressure sensors used at high temperatures.</p>
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 130 (1), 16-20, 2022-01-01
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390853567321504640
-
- NII論文ID
- 130008139223
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可