切削不要・微細表面構造を有する透明シリカガラス焼結体の作製

• 藤野 茂

  九州大学グローバルイノベーションセンター

書誌事項

タイトル別名

• Fabrication of Transparent Silica Glass by Powder Sintering Method Aiming Desired Shape Molding
• セッサク フヨウ ・ ビサイ ヒョウメン コウゾウ オ ユウスル トウメイ シリカガラス ショウケツタイ ノ サクセイ

抄録

In this paper, we present a procedure for fabricating transparent silica glass that uses a mesoporous SiO₂-PVA(poly(vinyl alcohol)) nanocomposite as a silica glass precursor. By sintering the nanocomposite in air at 1100°C, monolithic trasnsparent silica glass was obtained with no crack. Micropatterns on the nanocomposite were fabricated by room-temperature imprinting. Micropatterned silica glass was obtained by sintering the nanocomposite at 1100°C in air. The sintered glass possessed various color photoluminescence (PL) under UV irradiation, depending on the kind of rare earth and transition metal ions.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 69 (2), 73-77, 2022-02-15

  一般社団法人 粉体粉末冶金協会

キーワード

• silica glass
• powder sintering
• mesoporous; SiO₂-PVA nanocomposite
• photoluminescence

詳細情報

• CRID: 1390854064975446144
• NII論文ID: 130008160382
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.69.73
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 031998405
• Web Site: http://id.ndl.go.jp/bib/031998405
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I031998405
• Web Site: https://www.jstage.jst.go.jp/article/jjspm/69/2/69_73/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
  • KAKEN
• 抄録ライセンスフラグ: 使用不可