Fabrication of 6,13-Bis(triisopropylsilylethynyl) Pentacene Films by Electrostatic Spray Deposition for Bottom-Contact Organic Field-Effect Transistors

• Norio Onojima

• Naomichi Nishio

• Takamasa Kato

抄録

In this study, 6,13-bis(triisopropylsilylethynyl) pentacene (TIPS pentacene) films were prepared by electrostatic spray deposition (ESD) for fabrication of bottom-contact organic field-effect transistors (OFETs) having the channel length of 5 µm. Since the crystalline quality of TIPS pentacene film strongly depends on the nature of the spray droplets, we investigated preparation condition of TIPS pentacene solution with mixed organic solvents. Large crystal domains were obtained by using a 1,2-diclorobenzene ( o -DCB):ethanol mixed solvent. On the other hand, the film deposited using the toluene:ethanol mixed solvent was composed of small domains. Due to larger crystal domains obtained in the film deposited using the o -DCB:ethanol mixed solvent (i.e., reducing domain boundaries), we could fabricate the bottom-contact OFET exhibiting the field-effect mobility of 1.6×10 -2 cm 2 /(V·s) which was almost 100 times higher than that based on the film deposited using the toluene:ethanol mixed solvent [2.0×10 -4 cm 2 /(V·s)].

収録刊行物

• Japanese Journal of Applied Physics

  Japanese Journal of Applied Physics 52 (5S1), 05DB06-, 2013-05-01

  IOP Publishing

キーワード

• General Physics and Astronomy
• General Engineering

詳細情報

• CRID: 1360284924863559936
• NII論文ID: 210000142211
• DOI: 10.7567/jjap.52.05db06
• ISSN: 13474065
• ISSN: 00214922
• ISSN: http://id.crossref.org/issn/13474065
• Web Site: https://iopscience.iop.org/article/10.7567/JJAP.52.05DB06
• Web Site: https://iopscience.iop.org/article/10.7567/JJAP.52.05DB06/pdf
• データソース種別:
  • Crossref
  • CiNii Articles