Formation of Morphotropic Phase Boundary in (Na<sub>0.5</sub>K<sub>0.5</sub>)NbO<sub>3</sub>–BaZrO<sub>3</sub>–(Bi<sub>0.5</sub>Li<sub>0.5</sub>)TiO<sub>3</sub> Lead-Free Piezoelectric Ceramics
抄録
<jats:p> For the development of lead-free piezoelectric ceramics, which have a tetragonal–rhombohedral morphotropic phase boundary (MPB), 0.90(Na<jats:sub>0.5</jats:sub>K<jats:sub>0.5</jats:sub>)NbO<jats:sub>3</jats:sub>–<jats:italic>x</jats:italic>BaZrO<jats:sub>3</jats:sub>–(0.10 - <jats:italic>x</jats:italic>)(Bi<jats:sub>0.5</jats:sub>Li<jats:sub>0.5</jats:sub>)TiO<jats:sub>3</jats:sub> ceramics have been synthesized by the conventional solid state reaction method. A phase diagram was summarized from the X-ray diffraction pattern and the dielectric measurements. It is found that 0.90(Na<jats:sub>0.5</jats:sub>K<jats:sub>0.5</jats:sub>)NbO<jats:sub>3</jats:sub>–<jats:italic>x</jats:italic>BaZrO<jats:sub>3</jats:sub>–(0.10 - <jats:italic>x</jats:italic>)(Bi<jats:sub>0.5</jats:sub>Li<jats:sub>0.5</jats:sub>)TiO<jats:sub>3</jats:sub> ceramics have an MPB between <jats:italic>x</jats:italic> = 0.07 and 0.08. In the vicinity of the MPB, it was observed that the dielectric and piezoelectric properties were enhanced. </jats:p>
収録刊行物
-
- Japanese Journal of Applied Physics
-
Japanese Journal of Applied Physics 52 (7S), 07HB02-, 2013-06-20
IOP Publishing
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1360566399840692608
-
- NII論文ID
- 210000142474
-
- ISSN
- 13474065
- 00214922
- http://id.crossref.org/issn/13474065
-
- データソース種別
-
- Crossref
- CiNii Articles