Crystal structure instability of FeSe grains: Formation of non-superconducting phase at the grain surface
抄録
<jats:title>Abstract</jats:title> <jats:p>We investigated the magnetization and crystal structure of FeSe polycrystalline samples with various grain sizes. For the samples with large grains, a large magnetic critical current density <jats:italic>J</jats:italic> <jats:sub>c</jats:sub> was observed. For the samples with small grains, superconductivity signals were not observed; instead, magnetization hysteresis, which is not a result of superconductivity, was observed. In the X-ray diffraction pattern for the samples with small grains, broad additional peaks were observed, corresponding to the formation of the non-superconducting (monoclinic) Fe–Se phase at the FeSe grain surface. The crystal structure instability at the grain surface would be the reason for the low superconducting properties of the Fe-chalcogenide polycrystalline wires investigated thus far.</jats:p>
収録刊行物
-
- Japanese Journal of Applied Physics
-
Japanese Journal of Applied Physics 55 (5), 053101-, 2016-04-01
IOP Publishing
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1360003449890496640
-
- NII論文ID
- 210000146460
-
- ISSN
- 13474065
- 00214922
-
- データソース種別
-
- Crossref
- CiNii Articles
- KAKEN