抄録
In immiscible blends of poly(2-ethylhexyl acrylate-co-acrylic acid-co-vinyl acetate) P(2EHA-AA-VAc) with poly(vinylidene fluoride-co-hexafluoroacetone) P(VDF-HFA), depth profiling was carried out by PAS-FTIR and ATR-FTIR analyses. Integrated surface excesses of P(VDF-HFA) component (φ1) in blends were plotted against depth for P(2EHA-AA-VAc)/P(VDF-HFA) (50/50), (30/70), and (10/90) blends. In all blends, since φ1 decreased with increasing depth, it was expected that P(2EHA-AA-VAc)/P(VDF-HFA) blends would be gradient materials (surface segregation structures). Furthermore, at a few nm depth from the surface, XPS analysis was done to get more detailed information of the surface. We point out that PAS-FTIR is very effective analysis to get depth profiling in such immiscible polymer blends as P(2EHA-AA-VAc)/P(VDF-HFA).
収録刊行物
-
- Polymer Journal
-
Polymer Journal 27 (4), 339-346, 1995
The Society of Polymer Science, Japan
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681266113280
-
- NII論文ID
- 130004429654
- 30001926857
-
- COI
- 1:CAS:528:DyaK2MXltFSlu7s%3D
-
- ISSN
- 13490540
- 00323896
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可