Grain-boundary enhanced interdiffusion in polycrystalline CaO-stabilized zirconia system
-
- Y. Oishi
- Department of Nuclear Engineering, Kyushu University, Fukuoka 812, Japan
-
- H. Ichimura
- Department of Nuclear Engineering, Kyushu University, Fukuoka 812, Japan
抄録
<jats:p>A solution of the flux density equation is presented for grain−boundary enhanced diffusion in a polycrystalline system when the penetration depth is large relative to the grain size. The solution is applied to interdiffusion between 13 and 19 mol% CaO-stabilized zirconia polycrystals from 1375–1650 °C. Lattice interdiffusion coefficients calculated from the concentration distributions are slightly larger than the previously reported self-diffusion coefficients of the individual cations.</jats:p>
収録刊行物
-
- The Journal of Chemical Physics
-
The Journal of Chemical Physics 71 (12), 5134-5139, 1979-12-15
AIP Publishing
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1362544419907539584
-
- NII論文ID
- 30015672998
-
- DOI
- 10.1063/1.438286
-
- ISSN
- 10897690
- 00219606
-
- データソース種別
-
- Crossref
- CiNii Articles