- Z. Altounian
- Department of Physics, McGill University, Montreal, Quebec H3A 2T8, Canada
-
- D. H. Ryan
- Department of Physics, McGill University, Montreal, Quebec H3A 2T8, Canada
-
- G. H. Tu
- Department of Physics, McGill University, Montreal, Quebec H3A 2T8, Canada
この論文をさがす
抄録
<jats:p>A new metastable compound has been obtained during the crystallization of Fe-rich Nd-Fe-B amorphous alloys. The composition range for the precipitation of this phase is Nd4.5±1Fe82.5±5B12.5±3.5. A single phase, however, is obtained in a much restricted composition range. The amorphous alloy has a Curie temperature of 466 K and crystallizes at 852 K (for a heating rate of 40 K min−1 ) into the new metastable compound which has a body-centered-cubic structure with a=1.238 nm. Its Curie temperature is 548 K. Upon heating above 975 K, this phase transforms into Nd2Fe14B, NdFe12B6, and α-Fe. It appears that it is necessary to start from a truly amorphous state in order to form the new phase, otherwise, a competing body-centered-cubic phase Nd2Fe23B3 forms. X-ray diffraction and Mössbauer spectroscopy data are also presented and compared to that of Nd2Fe23B3.</jats:p>
収録刊行物
-
- Journal of Applied Physics
-
Journal of Applied Physics 64 (10), 5723-5725, 1988-11-15
AIP Publishing
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1363670320478438144
-
- NII論文ID
- 30015833876
-
- NII書誌ID
- AA00693547
-
- DOI
- 10.1063/1.342238
-
- ISSN
- 10897550
- 00218979
-
- データソース種別
-
- Crossref
- CiNii Articles