抄録
<jats:p>The permittivity of single-crystal single-domain strontium titanate has been measured in detail in the [001], [011], and [111] directions, as a function of temperature (from 4.2 to 300 °K), electric field (from −23 000 to +23 000 V/cm, and frequency (from 1 kHz to 50 MHz). The free energy of the crystal is determined as a function of polarization with temperature as a parameter. The Curie-Weiss law is satisfied in the temperature range 60–300 °K, giving a Curie temperature of 30 ± 2 °K for the three crystal orientations. The Lyddane-Sachs-Teller (LST) relation is satisfied for temperatures between 30 and 300 °K and for electric fields between 0 and 12 000 V/cm. A generalized LST relation is used to calculate the permittivity of strontium titanate from zero to optic frequencies. Two active optic modes are important. The lower-frequency mode is attributed mainly to motion of the strontium ions with respect to the rest of the lattice, while the higher-frequency active mode is attributed to motion of the titanium ions with respect to the oxygen lattice. The restoring forces that act on the Ti ions begin to ``harden'' when these ions are displaced approximately 0.002 Å from their equilibrium positions.</jats:p>
収録刊行物
-
- Journal of Applied Physics
-
Journal of Applied Physics 43 (5), 2124-2131, 1972-05-01
AIP Publishing
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1360574096152378112
-
- NII論文ID
- 30015885722
-
- NII書誌ID
- AA00693547
-
- ISSN
- 10897550
- 00218979
-
- データソース種別
-
- Crossref
- CiNii Articles