TiO2 Nanoparticle Suspension Preparation Using Ultrasonic Vibration-Assisted Arc-Submerged Nanoparticle Synthesis System (ASNSS)
-
- Chang Ho
- Department of Mechanical Engineering, National Taipei University of Technology
-
- Tsung Tsing-Tshih
- Department of Mechanical Engineering, National Taipei University of Technology
-
- Chen Liang-Chia
- Institute of Automation Technology, National Taipei University of Technology
-
- Yang Yi-Cheng
- Department of Mechanical Engineering, National Taipei University of Technology
-
- Lin Hong-Ming
- Department of Materials Engineering, Tatung University
-
- Han Lee-Long
- Department of Mechanical Engineering, National Taipei University of Technology
-
- Lin Chung-Kwei
- Department of Material Science, Feng Chia University
書誌事項
- タイトル別名
-
- TiO<SUB>2</SUB> Nanoparticle Suspension Preparation Using Ultrasonic Vibration-Assisted Arc-Submerged Nanoparticle Synthesis System (ASNSS)
この論文をさがす
抄録
This paper proposes a new method—the ultrasonic vibration-assisted arc-submerged nanoparticle synthesis system for preparing TiO2 nanoparticle preparation. In addition to the influence of the ultrasonic amplitude and various process variables such as breakdown voltage, pulse duration, current, and dielectric liquid temperature on particles, this paper will also discuss the relationship between the pH value and the surface potential of the suspension. Experimental results have shown that the proposed method can successfully prepare anatase type TiO2. The TEM image further shows a mean particle size below 10 nm, and that nanoparticle suspension cannot reach a state of stable suspension and starts aggregating under a pH value below 6.4.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 45 (3), 806-811, 2004
公益社団法人 日本金属学会
- Tweet
詳細情報
-
- CRID
- 1390282679228242816
-
- NII論文ID
- 10012717129
- 30018851117
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2cXjsVGru7o%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6899125
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可