Adsorption Property of Water Vapor on AlPO₄-5 Synthesized from Aluminum Dross
-
- Murayama Norihiro
- Department of Chemical, Energy and Environmental Engineering, Kansai University School of Chemical and Biomolecular Engineering, The University of Sydney
-
- Baba Makoto
- Department of Chemical, Energy and Environmental Engineering, Kansai University
-
- Hayashi Jun-ichi
- Department of Chemical, Energy and Environmental Engineering, Kansai University
-
- Shibata Junji
- Department of Chemical, Energy and Environmental Engineering, Kansai University
-
- Valix Marjorie
- School of Chemical and Biomolecular Engineering, The University of Sydney
書誌事項
- タイトル別名
-
- Adsorption Property of Water Vapor on AlPO<sub>4</sub>-5 Synthesized from Aluminum Dross
この論文をさがす
抄録
The aluminophosphate type zeolitic material, AlPO4-5 was synthesized by hydrothermal method using aluminum dross as a raw material, and its water vapor adsorption property was studied. Porous AlPO4-5 and nonporous AlPO4 were formed, and the selectivity of their formation was determined by varying the reactant ratios. Both AlPO4-5 and tridymite type AlPO4 (nonporous phosphate) were obtained from aluminum dross when the reaction products were synthesized with the following composition, Al2O3 : P2O5 : triethylamine (TEA) : H2O = 1 : 1 : 1 : 40. While AlPO4-5 was preferentially synthesized as a main product when the compositions were Al2O3 : P2O5 : TEA : H2O = 2 : 1 : 1 : 40 and 1 : 1 : 2 : 40. The variation in the reactant ratio dictated the specific surface area of the resulting reaction products. The formation of AlPO4-5 with a composition of 1 : 1 : 2 : 40 generated surface area of 353 m2/g. The reaction products synthesized at 2 : 1 : 1 : 40 and 1 : 1 : 1 : 40 generated surface areas of 187 and 75 m2/g, respectively. All the aluminophosphate products exhibited the type IV or V isotherm by IUPAC classification for water vapor adsorption due to the AlPO4-5 pore with strong affinity. This study demonstrated the efficacy of AlPO4-5 obtained from aluminum dross as desiccant, that is, the aluminum dross-derived AlPO4-5 demonstrated high adsorption capacity and adsorption properties suitable as an adsorbent or a desiccant.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (12), 2265-2270, 2013
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204250198272
-
- NII論文ID
- 40019890271
- 130004455028
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC2cXitFekurc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025048454
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可