Performance Enhancement of Rechargeable Sulfur Cathode Utilizing Microporous Activated Carbon Composite
-
- OKABE Sota
- Department of Chemistry and Materials Engineering, Faculty of Chemistry, Materials and Bioengineering, Kansai University
-
- UCHIDA Satoshi
- Department of Chemistry and Materials Engineering, Faculty of Chemistry, Materials and Bioengineering, Kansai University
-
- MATSUI Yukiko
- Department of Chemistry and Materials Engineering, Faculty of Chemistry, Materials and Bioengineering, Kansai University
-
- YAMAGATA Masaki
- Department of Chemistry and Materials Engineering, Faculty of Chemistry, Materials and Bioengineering, Kansai University
-
- ISHIKAWA Masashi
- Department of Chemistry and Materials Engineering, Faculty of Chemistry, Materials and Bioengineering, Kansai University
この論文をさがす
抄録
We prepared activated carbon (AC) and sulfur (S) composite cathodes. The present AC has developed micropores and a large pore volume. The composite could successfully include a large amount of S and exhibited stable cycle performance in a glyme-based electrolyte. An oxidation treatment of the AC with a concentrated nitric acid solution at 120°C was found to improve S utilization in charge-discharge cycling. A cathode with the oxidized AC including S showed stable cycle performance with a high capacity in not only the glyme-based electrolyte but also a carbonate-based electrolyte.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 85 (10), 671-674, 2017
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681476969472
-
- NII論文ID
- 130006138818
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 028553348
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用可