- Kato Takahiro
- Faculty of Engineering and Resource Science, Akita University
-
- Takada Yuri
- Faculty of Engineering and Resource Science, Akita University
-
- Okawa Hirokazu
- Faculty of Engineering and Resource Science, Akita University
-
- Sugawara Katsuyasu
- Faculty of Engineering and Resource Science, Akita University
この論文をさがす
抄録
<p>Copper fine particles were prepared by a wet chemical method using copper sulfate as a starting material, hydrazine as a reducing agent, and sodium hydroxide as a pH adjuster. It was found that there was a branch point at which the precursor changed to copper hydroxide (Cu(OH)2) or copper oxide (CuO), depending on the sodium hydroxide/copper sulfate molar ratio, and a range in which the particle size of the metallic copper fine particles was minimum. At higher concentrations and feeding rates of the hydrazine solution, smaller copper particles were obtained. Copper particles with a size of 0.14–2.4 µm were obtained at a sodium hydroxide/copper sulfate molar ratio of 0.9–4.9, hydrazine concentration of 2.02–20.2 mol/L, and hydrazine feeding rate of 0.5–1.0 mL/min.</p>
収録刊行物
-
- JOURNAL OF CHEMICAL ENGINEERING OF JAPAN
-
JOURNAL OF CHEMICAL ENGINEERING OF JAPAN 54 (3), 103-109, 2021-03-20
公益社団法人 化学工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390568916164044288
-
- NII論文ID
- 130008000735
-
- NII書誌ID
- AA00709658
-
- ISSN
- 18811299
- 00219592
-
- NDL書誌ID
- 031352476
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可