FTIR studies on the structure of silane coupling agents reacted with glass surface ガラス表面で反応したシランカップリング剤の構造に関する研究 : フーリエ変換赤外分光法の応用
Access this Article
Search this Article
Author
Bibliographic Information
- Title
-
FTIR studies on the structure of silane coupling agents reacted with glass surface
- Other Title
-
ガラス表面で反応したシランカップリング剤の構造に関する研究 : フーリエ変換赤外分光法の応用
- Author
-
西尾, 悦雄
- Author(Another name)
-
ニシオ, エツオ
- University
-
名古屋工業大学
- Types of degree
-
工学博士
- Grant ID
-
乙第28号
- Degree year
-
1991-06-06
Note and Description
博士論文
Table of Contents
- CONTENTS / p1 (0007.jp2)
- CHAPTER 1 Introduction / p1 (0008.jp2)
- 1.1 The Significance of the Analysis of Silane Coupling Agents on Inorganic Materials / p2 (0009.jp2)
- 1.2 The Application of Fourier Transform Infrared Spectroscopy (FTIR) to Silane Coupling Agent Analysis / p5 (0011.jp2)
- 1.3 References / p32 (0024.jp2)
- CHAPTER 2 Analysis of Silane Coupling Agents by Pyro-GC/FTIR / p34 (0025.jp2)
- 2.1 Introduction / p35 (0026.jp2)
- 2.2 Experimental / p38 (0028.jp2)
- 2.3 Results and Discussion / p41 (0029.jp2)
- 2.4 Conclusion / p62 (0040.jp2)
- 2.5 References / p63 (0040.jp2)
- CHAPTER 3 Characterization of Silane Coupling Agents on the Surface of Silicate / p65 (0041.jp2)
- 3.1 Introduction / p66 (0042.jp2)
- 3.2 Experimental / p70 (0044.jp2)
- 3.3 Results and Discussion / p74 (0046.jp2)
- 3.4 Conclusion / p99 (0059.jp2)
- 3.5 References / p100 (0059.jp2)
- CHAPTER 4 Analysis of Keratin Bound on Silica Gel with Silane Coupling Agent / p101 (0060.jp2)
- 4.1 Introduction / p102 (0061.jp2)
- 4.2 Experimental / p108 (0064.jp2)
- 4.3 Results and Discussion / p114 (0067.jp2)
- 4.4 Conclusion / p148 (0084.jp2)
- 4.5 References / p149 (0085.jp2)
- CHAPTER 5 Silane Coupling Agent Effect on Mechanical Properties of Glass Fibers / p151 (0086.jp2)
- 5.1 Effect of Silane Coupling Agent on Fracture Process / p152 (0087.jp2)
- 5.2 Effect of Silane Bonding State on Interfacial Strength / p169 (0096.jp2)
- 5.3 Conclusion / p189 (0106.jp2)
- 5.4 References / p190 (0106.jp2)
- CHAPTER 6 Conclusion / p191 (0107.jp2)
- Acknowledgements / p195 (0110.jp2)