Forming processing for nonplastic materials 非塑性材料の成形加工に関する研究
この論文にアクセスする
この論文をさがす
著者
書誌事項
- タイトル
-
Forming processing for nonplastic materials
- タイトル別名
-
非塑性材料の成形加工に関する研究
- 著者名
-
陳, 湘明
- 著者別名
-
チェン, シアンミン
- 学位授与大学
-
東京大学
- 取得学位
-
工学博士
- 学位授与番号
-
甲第9039号
- 学位授与年月日
-
1991-03-29
注記・抄録
博士論文
目次
- Contents / p1 (0004.jp2)
- 1 Introduction / p1 (0007.jp2)
- 1.1 Background / p1 (0007.jp2)
- 1.2 Heterogeneities Related to Powder Processing / p2 (0008.jp2)
- 1.3 Recent Development of Powder Processing / p3 (0009.jp2)
- 1.4 Hot Working of Ceramics / p5 (0011.jp2)
- 1.5 Cold-Working and Annealing Process for Ceramics / p8 (0014.jp2)
- 2 Forming of Metal Sheathed Alumina Wires by Controlled Fracture Forming Process / p17 (0023.jp2)
- 2.1 Introduction / p17 (0023.jp2)
- 2.2 Outline of Process and Experimental Details / p18 (0024.jp2)
- 2.3 Failure in Sheath Material and Forming Limit / p24 (0030.jp2)
- 2.4 Reductions of Sheath and Ceramic Workpiece / p27 (0033.jp2)
- 2.5 Density Variation and Evaluation of Formed Materials / p31 (0037.jp2)
- 2.6 Resintering / p37 (0043.jp2)
- 2.7 Discussion and Conclusion / p41 (0047.jp2)
- 3 Control of Density of Ceramic Wires During Controlled Fracture Forming Process / p45 (0051.jp2)
- 3.1 Introduction / p45 (0051.jp2)
- 3.2 Modeling for Change of Mass Density / p46 (0052.jp2)
- 3.3 Experimental Procedure / p49 (0055.jp2)
- 3.4 Consolidation Behavior / p53 (0059.jp2)
- 3.5 Control of Density by Improving Constraint Condition / p57 (0063.jp2)
- 3.6 Discussion / p59 (0065.jp2)
- 3.7 Conclusion / p63 (0069.jp2)
- 4 Resintering Characteristic of Ceramics after Cold-Working / p65 (0071.jp2)
- 4.1 Introduction / p65 (0071.jp2)
- 4.2 Experimental Procedure / p66 (0072.jp2)
- 4.3 Effects of Particle Arrangement on Sinterability / p71 (0077.jp2)
- 4.4 Densification Characteristics of Alumina Wires / p79 (0085.jp2)
- 4.5 Conclusion / p82 (0088.jp2)
- 5 Controlled Fracture Forming Process for Nickel Sheathed Alumina Plates / p87 (0093.jp2)
- 5.1 Introduction / p87 (0093.jp2)
- 5.2 Experimental Procedure / p88 (0094.jp2)
- 5.3 Forming Conditions and Formability / p90 (0096.jp2)
- 5.4 Fracture Behavior of Alumina and Evaluation of Formed Plates / p96 (0102.jp2)
- 5.5 Resintering of Alumina Plates / p102 (0108.jp2)
- 5.6 Discussion / p105 (0111.jp2)
- 5.7 Conclusion / p107 (0113.jp2)
- 6 Microstructure Refining of Alumina by Cold-Working and Annealing Process / p110 (0116.jp2)
- 6.1 Introduction / p110 (0116.jp2)
- 6.2 Experimental Procedure / p112 (0118.jp2)
- 6.3 Improvement in Porosity Structure / p112 (0118.jp2)
- 6.4 Grain Refining / p120 (0126.jp2)
- 6.5 Discussion / p126 (0132.jp2)
- 6.6 Conclusion / p128 (0134.jp2)
- 7 General Conclusion / p131 (0137.jp2)
- Acknowledgement / p135 (0141.jp2)