Transmission electron microscopy study on mechanisms of deformation and fracture in ceramics セラミックスにおける変形および破壊機構に関する透過電子顕微鏡的研究
Access this Article
Search this Article
Author
Bibliographic Information
- Title
-
Transmission electron microscopy study on mechanisms of deformation and fracture in ceramics
- Other Title
-
セラミックスにおける変形および破壊機構に関する透過電子顕微鏡的研究
- Author
-
文, 元振
- Author(Another name)
-
ムン, ワンジン
- University
-
名古屋大学
- Types of degree
-
博士 (工学)
- Grant ID
-
甲第4725号
- Degree year
-
2000-03-27
Note and Description
博士論文
Table of Contents
- CONTENTS / (0003.jp2)
- CHAPTER1 INTRODUCTION / p1 (0006.jp2)
- 1.1 Background of the present study / p1 (0006.jp2)
- 1.2 MGC materials and DS-Al₂O₃/YAG eutectic ceramic / p3 (0008.jp2)
- 1.3 The aim of the present study / p5 (0010.jp2)
- 1.4 Crystallography of each phase in DS-A1₂O₃/YAG eutectic ceramic / p9 (0014.jp2)
- References / p15 (0020.jp2)
- CHAPTER2 DISLOCATIONS IN YAG PHASE OF A DS-A1₂O₃/YAG EUTECTIC CERAMIC DEFORMED AT ROOM AND HIGH TEMPERATURES / p17 (0022.jp2)
- 2.1 Introduction / p17 (0022.jp2)
- 2.2 Experimental procedures / p17 (0022.jp2)
- 2.3 Results and discussion / p21 (0026.jp2)
- 2.4 Conclusions / p43 (0048.jp2)
- References / p44 (0049.jp2)
- CHAPTER3 DISLOCATIONS IN α-Al₂O₃PHASE OF A DS-Al₂O₃/YAG EUTECTIC CERAMIC DEFORMED AT ROOM AND HIGH TEMPERATURES / p45 (0050.jp2)
- 3.1 Introduction / p45 (0050.jp2)
- 3.2 Experimental procedures / p45 (0050.jp2)
- 3.3 Results and discussion / p45 (0050.jp2)
- 3.4 Conclusions / p59 (0064.jp2)
- References / p62 (0067.jp2)
- CHAPTER4 TEM OBSERVATIONS AND MODELING OF HEALING OF A CRACK TIP IN YAG SINGLE CRYSTAL / p63 (0068.jp2)
- 4.1 Introduction / p63 (0068.jp2)
- 4.2 Experimental procedures / p63 (0068.jp2)
- 4.3 Results / p64 (0069.jp2)
- 4.4 Discussion and summary / p76 (0081.jp2)
- References / p81 (0086.jp2)
- CHAPTER5 TOUGHENING OF YAG SINGLE CRYATAL BY FORMATION OF DISLOCATION CELL STRUCTURE / p82 (0087.jp2)
- 5.1 Introduction / p82 (0087.jp2)
- 5.2 Experimental procedures / p84 (0089.jp2)
- 5.3 Results / p85 (0090.jp2)
- 5.4 Discussion / p92 (0097.jp2)
- 5-5 Conclusions / p92 (0097.jp2)
- References / p94 (0099.jp2)
- CHAPTER6 SUMMARY / p95 (0100.jp2)