The mechanisms of metallurgical failure : on the origin of fracture

著者

    • Campbell, John

書誌事項

The mechanisms of metallurgical failure : on the origin of fracture

John Campbell

Butterworth-Heinemann, 2020

  • pbk.

大学図書館所蔵 件 / 全2件

この図書・雑誌をさがす

内容説明・目次

内容説明

Metallurgy of Fracture: The Mechanics of Metal Failure looks at the origin of metal defects, their related mechanisms of failure, and the modification of casting procedures to eliminate these defects, clearly connecting the strength and durability of metals with their fabrication process. The book starts with a focus on the fracture of liquids, looking at topics such as homogeneous and heterogeneous nucleation, entrainment processes in bifilms and bubbles, furling and unfurling, ingot casting, continuous casting, and more. From there it discusses fracture of liquid and solid state, focusing on topics such as externally and internally initiated tearing. The book then concludes with a section discussing fracture of solid metals covering concepts such as ductility and brittleness, dislocation mechanisms, the relationship between the microstructure and properties of metals, corrosion, hydrogen embrittlement, and more. Improved approaches to fabrication and casting processes that will help eliminate these defects are provided throughout.

目次

1. Theoretical Strength of Liquids2. Non-Classical Mechanisms of Fracture in Metals3. Experimental Hydrostatic Tensions in Liquids4. Entrainment Processes5. Entrainment Avoidance6. The Quest for Clean Steels7. Externally Initiated Tearing8. Internally Initiated Tearing9. The Concepts of Ductility and Brittleness10. Theoretical Strength of the Solid11. Theoretical Strength Summary12. Consolidation13. Microstructure and Properties of Metals

「Nielsen BookData」 より