  • A Coherent Phase Diagram of the [(AuCu)_<0.86>Ag_<0.14>]_<1-X>Pt_X Pseudobinary Section in Au-Cu-Ag-Pt Quaternary System

    SAKRANA Amal Abd El Samad , TANAKA Yasuhiro , UDOH Kouichi , HISATSUNE Kunihiro , ATSUTA Mitsuru , YASUDA Katsuhiro

    In order to determine a coherent phase diagram of the [(AuCu)<sub>0.86</sub>Ag<sub>0.14</sub>]<sub>1-X</sub>Pt<sub>X</sub> pseudobinary system, phase id …

    Dental Materials Journal 16(2), 144-155, 1997-12-25

    J-STAGE  NDL Digital Collections  Ichushi Web  References (18)

  • Anisotropic Expansion in Gypsum-bonded Cristobalite Investment Mold

    SHIBUYA Masafumi , OHSAWA Masahiro , MATSUMOTO Hiroshi , HISATSUNE Kunihiro , YASUDA Katsuhiro

    Expansion of a gypsum-bonded investment mold was investigated using a fused quartz tube pattern. Two hours after mixing, a fusible alloy was cast into the space around the pattern induced by setting e …

    Dental Materials Journal 16(1), 48-59, 1997-06-25

    J-STAGE  NDL Digital Collections  Ichushi Web  References (18)

  • Aging behaviour in a dental low gold alloy with high copper content  [in Japanese]

    HAMASAKI K. , HISATSUNE K. , NARUSE S. , UDOH K. , TANAKA Y. , YASUDA K.

    歯科材料・器械 16(29), 47, 1997-03-20

    Ichushi Web  References (3)

  • High resolution electron microscopy of the interface for porcelain-gold alloy bonding  [in Japanese]

    TANAKA Y. , UDOH K. , HISATSUNE K. , YASUDA K. , NAGANO S. , BABA K. , Van LANDUYT J. , Van TENDELOO G.

    歯科材料・器械 16(29), 110, 1997-03-20

    Ichushi Web  Cited by (2)

  • Fatigue resistance of composite restorations as influenced by inorganic filler particle size

    HTANG A. , OHSAWA M. , MATSUMOTO H. , YASUDA K.

    A series of experimental composites containing quartz particles(75wt%)in a resin matrix of Bis-GMA/TEGDMA was evaluated for its fatigue resistance.The filler particle sizes in the materials were class …

    歯科材料・器械 14(26), 128-129, 1995-09-05

  • Effect of water - to - powder ratio on thermal expansion of a gypsum - bonded investment for quick heating  [in Japanese]

    SHIRAISHI C. , SHIBUYA M. , OHSAWA M. , HISATSUNE K. , YASUDA K.

    混水比が急速加熱型石膏系埋没材の熱膨張量に及ぼす影響について、円柱試験片を用いて検討した。その結果、700℃における加熱膨張量は、混水比の増加にしたがって減少した。また、未加熱硬化体の見かけの密度も同様の傾向であり、混水比による加熱膨張量の変化は、硬化体の空隙率の影響によることが明らかになった。

    歯科材料・器械 14(26), 262-263, 1995-09-05

    Ichushi Web  References (1)

  • Abnormal Behavior in Adiabatic Calorimetry of Set Dental Stone

    HISATSUNE Kunihiro , EL ARABY M. , IWANUMA Kenji , TANAKA Yasuhiro , UDOH Koichi , YASUDA Katsuhiro

    Dehydration in set dental stone was studied by employing specific heat measurements. Dehydration proceeds in two steps in air. In the case of bulk samples, especially those made with a lower water-pow …

    Dental Materials Journal 14(1), 84-87, 1995-06-25

    J-STAGE  NDL Digital Collections  References (5)

  • Fatigue resistance of composite resin as influenced by filler content  [in Japanese]

    HTANG A. , OHSAWA M. , MATSUMOTO H. , YASUDA K.

    疲労強度に及ぼすフィラー含有量の影響を調べた。光重合型のベースレジンにシラン処理された石英フィラー(粒径3〜5μm)を40〜85wt%含有する6種のレジンを準備し、牛歯に形成された規格窩洞に〓塞した。5〜15×10^4回の繰り返し衝撃荷重を負荷した。試片切断面で、生じたクラックを顕微鏡的に調べた。その結果、フィラー含有量75%のものが最も優れた疲労強度を示し、60%以下および80%以上のものは劣っ …

    歯科材料・器械 14(25), 90-91, 1995-03-31

    Cited by (1)

  • Setting and thermal expansion of various gypsum-bonded investment for quick heating  [in Japanese]

    SHIBUYA M. , OHSAWA M. , MATSUMOTO H. , HISATSUNE K. , YASUDA K.

    各種市販されている急速加熱型石膏系埋没材について、練和開始から120分までの硬化膨張曲線および室温から0.5℃/minで700℃まで加熱した場合の熱膨張曲線を求め、その特徴について比較検討した。その結果、練和開始から30分後の硬化膨張量、加熱膨張量は製品によって様々であり、石膏、シリカの成分比にも違いがあることが判った。

    歯科材料・器械 14(25), 126-127, 1995-03-31

  • Age-harding mechanisume of the [Aux-(Ag_<0.24>Cu_<0.76>)_1_-x]_<0.985>-Pt_<0.015> section in the Au-Cu Ag-Pt quaternary system  [in Japanese]

    IWANUMA K. , GOTOH J. , UDOH K. , TANAKA Y. , HISATSUNE K. , YASUDA K.

    [AU_X-(Ag0.24Cu0.76)_<1-X>]_<0.985>-Pt_<0.015>系のAu濃度をX=0.523, 0.423, 0.269とした4種類の合金について、決定したコヒーレント状態図をもとに、時効硬化特性と相変態過程の関係を検討した結果、時効硬化は核生成・成長気孔により生ずるもの、スピノーダル分解機構によって生ずるものの、それぞれの温度・組成 …

    歯科材料・器械 14(25), 138-139, 1995-03-31

    References (2)

  • Effects of Elapsed Time and Heating Rate on Dimensional Change of a Gypsum-bonded Investment for Quick Heating  [in Japanese]

    SHIBUYA Masafumi , OHSAWA Masahiro , MATSUMOTO Hiroshi , HISATSUNE Kunihiro , YASUDA Katsuhiro

    This study investigated the effects of elapsed time and heating rate on dimensional change of a gypsum-bonded investment for quick heating by placing a mold directly in an electric furnace at 700℃.< …

    The Journal of the Japanese Society for Dental Materials and Devices 14(2), 193-197, 1995

    J-STAGE  Ichushi Web  References (14) Cited by (8)

  • Coherent phase diagram of the [Au_X-(Ag_<0.24>Cu_<0.76>)_<1-X>]_<0.985>-Pt_<0.015> section in the Au-Cu-Ag-Pt quaternary system  [in Japanese]

    IWANUMA K. , UDOH K. , TANAKA Y. , HISATSUNE K. , YASUDA K.

    [Au_X-(Ag_<0.24>Cu_<0.76>)_<1-X>]_<0.985>-Pt_<0.015>系のAu濃度をX=0.523, 0.423, 0.340, 0.269とした4種類の合金について、TEM観察およびSAED解析を行い、コヒーレント状態図を決定した。その結果、長周期規則構造を有するAuCu II規則相は形成されないこと、 …

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 13(特別号24), 48-49, 1994-09-05

  • Effects of elapsed time and heating rate on dimensional change of gypsum-bonded investment for quick heating  [in Japanese]

    SHIBUYA M. , OHSAWA M. , MATSUMOTO H. , HISATSUNE K. , YASUDA K.

    電気炉部分を可動式に改良した横型熱膨張計を用いて、加熱開始時期および加熱速度が急速加熱型石膏系埋没材の総膨張量に及ぼす影響について検討した。その結果、練和開始後50分までは総膨張量の増加がみられ、それ以降は同程度の膨張量であった。また、加熱速度の影響はほとんどみられなかった。

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 13(特別号24), 238-239, 1994-09-05

  • Preclinical evaluation of the gold alloy with age-hardenability at normal temperature  [in Japanese]

    WATANABE I. , FUNAKI K. , YAMASHITA N. , TANAGAWA M. , SAWASE T. , ATSUTA M. , HISATSUNE K. , YASUDA K.

    太田らは700℃で4分間溶体化処理することにより、口腔内温度において最初の2週間で約2倍の硬さに時効硬化するAuCu-6at% Ga合金を開発した^<1)>。この金合金を臨床応用する目的で、ブリッジの金型上での適合性について検討した結果、硬さの増加が最も大きい最初の時効が3、4日に収縮による変形が認められた。接着性レジンに対する接着強さはType IV金合金よりも有意に優っていた。また …

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 12(特別号22), 130-131, 1993-08-20

  • Effect of temperature gradient in the electric furnace on thermal expansion of the cristobalite mold  [in Japanese]

    SHIBUYA M. , OHSAWA M. , MATSUMOTO H. , HISATSUNE K. , YASUDA K.

    鋳型の加熱膨張の異方性に及ぼす電気炉内温度分布の影響について検討するために、電気炉内温度および鋳型内温度を三次元的に測定し、その温度勾配下における鋳型の膨張を石英管パターンを用いて調べた。その結果、鋳型内温度分布および鋳型の加熱膨張は電気炉内温度分布の影響を強く受け、炉内水平方向においてクリストバライト変態温度に早く達する部位の膨張がより大きいことが判った。

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 12(特別号22), 208-209, 1993-08-20

  • Effect of platinum addition on the ordering of equiatomic alloy AuCu(Part I)  [in Japanese]

    El-Araby A. , Iwanuma K. , Tanaka Y. , Udoh K. , Hisatsune K. , Yasuda K.

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 11(特別号19), 132-133, 1992-04-30

    Ichushi Web 

  • Anisotropic expansion of a cristobalite mould duving heating  [in Japanese]

    SHIBUYA M. , OHSAWA M. , MATSUMOTO H. , HISATSUNE K. , YASUDA K.

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 11(特別号19), 166-167, 1992-04-30

    Ichushi Web 

  • Effect of Platinum Addition on Phase Transformation to Au_X-(Ag_<0.24>Cu_<0.76>)_<1-X> Pseudobinary Alloys(1)  [in Japanese]

    IWANUMA K. , HISATSUNE K. , YASUDA K.

    18KAu(Au-36.5at%Cu-11.3at%Ag)合金に1.5at%Ptを添加した合金の時効硬化特性とその原因となる相変態機構について電気抵抗測定, 硬さ試験, X線回折, 電子顕微鏡直接観察により検討した.18KAu擬二元系合金の時効硬化は単調な1段階硬化であったのに対し, 本合金では2段階の硬化が見い出された.第1段階の硬化はAuCu I規則化核の分散強化, 第2段階は板状のAuCu …

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 10(特別号18), 167-168, 1991-09-25

    Ichushi Web 

  • Editorial News of Dental Materials Journal  [in Japanese]

    安田 克廣 , 久恒 邦博 , 小園 凱夫 , 松家 茂樹 , 宮崎 光治 , 太田 道雄

    Journal of the Japanese Society for Dental Materials and Devices 10(5), 708-709, 1991-09-25

  • P-51 AuCu-14at.%Ag合金の相変態における白金添加の影響  [in Japanese]

    谷 俊彦 , 安田 克廣

    本研究ではAuCu-14at.%Ag合金の相変態に対する白金添加の影響を明らかにするため(AuCu-14at.%Ag)_<1-x>Pt_x系合金について、電気抵抗測定、硬度測定、透過電子顕微鏡観察を行なった。その結果、白金を1.5at.%以上添加した合金でAuCuI型規則格子相の臨界温度の著しい上昇が確認された。また、AuCu-14at.%Ag合金で存在するAuCuII型規則格子相は観 …

    歯科材料・器械. Special issue, 日本歯科理工学会学術講演会講演集 10(特別号17), 194, 1991-04-25