Toshima H , Kaga M , Nezu T , Endo K , Saito M

Various tooth surface conditioners have been employed in the application of pit and fissure sealant material. We examined the adhesion strength of the resin-based sealant containing S-PRG filler bonde …

The journal of the Japanese Society for Dental Materials and Devices 34(5), 408, 2015-09-15

Ichushi Web 

Kaga M , Toshima H , Ida Y , Nagano-Takebe F , Nezu T , Endo K

To determine buffering capacity of glass ionomer cement materials, disks (n=3) of diameter 13 mm × 1 mm thick were immersed in 10 ml of lactic acid solution (pH 4.0) and incubated at 37℃ from 24 hours …

The journal of the Japanese Society for Dental Materials and Devices 33(5), 484, 2014-09-20

Ichushi Web 

KAKUDA S , KAGA M , IDA Y , TOSHIMA H , HASHIMOTO M , ENDO K , SANO H

Three marketed pit and fissure sealants were employed. They were cured in mold (dia.: 13mm, thickness: 1mm). And then the sealant specimen was put into pH4.0 solution (lactic acid aq.) together with a …

The journal of the Japanese Society for Dental Materials and Devices 32(2), 88, 2013-03-25

Ichushi Web  References (1)

TOSHIMA H , HASHIMOTO M , NAGANO F , KAGA M , ENDO K

The components of Portland cement (PC) are similar to that of mineral trioxide aggregate (MTA). MTA has been utilized for endodontic treatment due to its biocompatibility. The aim of this study was to …

The journal of the Japanese Society for Dental Materials and Devices 32(2), 85, 2013-03-25

Ichushi Web 

HASHIMOTO M , TOSHIMA H , YONEZAWA T , KAWAI K , KAGA M , ENDO K

This study evaluated biological responses of water-dispersible gold (Au-NPs) and silver nanoparticles (Ag-NPs) stabilized by metal-C σ-bonds in cultured murine macrophages (RAW264.7) using assay of ce …

The journal of the Japanese Society for Dental Materials and Devices 31(5), 356, 2012-09-25

Ichushi Web 

KAGA M , IDA Y , TOSHIMA H , HASHIMOTO M , ENDO Kazuhiko

Ion release and buffering capacity of functional filler-containing fissure sealants (FSs) were studied. Disks of 13 mm in diameter and 1 mm in thickness (n=4) were incubated for 24 hours into 5 ml lac …

The journal of the Japanese Society for Dental Materials and Devices 31(2), 172, 2012-03-25

Ichushi Web 

豊田 有希 , 阿部 亜美 , 星野 恵 , 吉原 俊博 , 加我 正行 , 八若 保孝

小児歯科学雑誌 48(5), 601, 2010-11-10

Ichushi Web  References (3)

HASHIMOTO M , IIJIMA M , NAGANO F , IDA Y , KAGA M , OHNO H , ENDO K

This study evaluated the chemical or structural changes of Si-based glass particles contained in cured resin polymers after long-term (150 and 300 days) test solution storage. Three types of glass par …

The journal of the Japanese Society for Dental Materials and Devices 29(5), 397, 2010-09-20

Ichushi Web  References (1)

源長 美知 , 加我 正行 , 増田 純子 , 八若 保孝

小児歯科学雑誌 48(2), 221, 2010-04-25

Ichushi Web  References (1)

SUGAI Makoto , MATSUDA Yasuhiro , NAGAYAMA Masato , KAGA Masayuki , YAWAKA Yasutaka

口腔内における歯質の脱灰，再石灰化を予測することは，齲蝕の発生，進行の予防，治療において重要である。Matsuda らは口腔内の連続的なpH 変化を再現することが可能な自動pH サイクル装置を開発し，その有効性を報告している。本研究では，自動pH サイクル装置を用いて乳歯および永久歯エナメル質の脱灰を比較検討した。試料は健全ヒト乳臼歯および健全ヒト第三大臼歯を厚さ約150 <i>μ&l …

The Japanese Journal of Pediatric Dentistry 48(1), 48-55, 2010-03-25