犀川 浩 , 原 正憲 , 渡辺 国昭 [他] , 水島 輝夫 , 諸住 正太郎
A 10mm cubic specimen cut from a chill-cast Mg-30%Ni-5%Y alloy block was vacuum-heated for 4 h at 873 K and was then examined under optical and electron microscopes to determine structural changes and …
Annual report of Hydrogen Isotope Research Center,Toyama University,Japan 26, 23-30, 2006
IR DOI
諸住 正太郎 , 井村 五郎 , 河野 紀雄 [他]
千葉工業大学プロジェクト研究年報 1, 81-83, 2004
MOROZUMI Shotaro , SAIKAWA Hiroshi , MIZUSHIMA Teruo
大会講演概要 102, 305-306, 2002-04-17
諸住 正太郎 , 河野 紀雄 , 佐藤 英一郎 [他]
千葉工業大学付属研究所研究報告 9, 85-87, 2002
MOROZUMI Shotaro , SAIKAWA Hiroshi , WATANABE Kuniaki
Cut pieces of cast Mg<sub>2</sub>Ni ingot were heated in a vacuum of about 10<sup>−2</sup> Pa for 1.8∼14.4 ks at 773, 823 and 873 K, and then examined using X-ray dif …
Journal of Japan Institute of Light Metals 51(1), 23-27, 2001-01-30
J-STAGE References (5)
MOROZUMI Shotaro , SAIKAWA Hiroshi
大会講演概要 98, 23-24, 2000-04-15
References (2)
MOROZUMI Shotaro , SAIKAWA Hiroshi , KOYAMA Kinichi , OTSUKI Masato
軽金属 49(10), 481-486, 1999-10-30
References (19)
諸住 正太郎
Metals & technology 69(10), 909-912, 1999-10
MOROZUMI S.
Metals & technology 69(9), 788-797, 1999-09
Cited by (3)
諸住 正太郎 , 大野 篤美 , (故)峯岸 知也 , 佐藤 英一郎 , 南和 一郎 , 中村 和彦 , 高谷 松文 , 井村 五郎 , 茂木 徹一 , 河野 紀雄 , 水島 輝夫 , 犀川 浩 , 山下 智司
軽金属 49(6), 263-269, 1999-06-30
References (4) Cited by (3)
Metals & technology 69(4), 349-352, 1999-04
Hatano Yuji , Tachikawa Tomoyuki , Mu Daobin , Abe Takayuki , Watanabe Kuniaki , Morozumi Shotaro
An amorphous MgNi alloy was prepared by mechanical alloying, and its charge/discharge characteristics were examined in a 6 M KOH solution at room temperature. The discharge capacity of the alloy was l …
Annual report of Hydrogen Isotope Research Center,Toyama University,Japan 19, 21-31, 1999
MOROZUMI Shotaro , SAIKAWA Hiroshi , KOYAMA Kinichi
大会講演概要 94, 263-264, 1998-05-01
Metals & technology 68(5), 426-428, 1998-05
Metals & technology 68(1), 5-12, 1998-01
HATANO Y. , KOBAYASHI Koji , MORI Katsunori , WATANABE Kuniaki , MOROZUMI Shotaro
The influence of pre-oxidation on charge/discharge characteristics of sintered Mg2Ni electrodes was examined with an open electrochemical cell. Mg2Ni powder was first oxidized slightly in air at 473 K …
Annual report of Hydrogen Isotope Research Center,Toyama University,Japan (18), 105-116, 1998
IR DOI Cited by (1)
MOROZUMI Shotaro , SAIKAWA Hiroshi , MINEGISHI Tomoya
大会講演概要 93, 3-4, 1997-10-20
SAIKAWA Hiroshi , MINEGISHI Tomoya , MOROZUMI Shotaro
A molten magnesium bath can be used for siliconizing of iron specimens embedded in SiC powder by keeping for 3.6ks at 1123K, to obtain an Fe<SUB>3</SUB>Si-SiC composite layer on the surfac …
Tetsu-to-Hagane 83(8), 508-513, 1997-08-01
J-STAGE References (2)
SAIKAWA Hiroshi , ONO Tohru , MINEGISHI Tomoya , MOROZUMI Shotaro
When a molten magnesium bath is used to siliconize iron and steel specimens embeded in SiC powder by keeping them in the bath for 3.6ks at 1123K, the siliconized layer obtained consists of two sublaye …
Tetsu-to-Hagane 83(8), 502-507, 1997-08-01
J-STAGE References (4)
A molten magnesium bath was used to siliconize iron and steel specimens embedded in SiC powder for various periods at 973-1123K. The siliconized layer obtained was composed of Fe<SUB>3</SUB&g …
Tetsu-to-Hagane 83(7), 442-447, 1997-07-01
J-STAGE References (7)