Tomokiyo Yoshitsugu , Kaku Kunio , Eguchi Tetsuo

Extended dislocation nodes in αCu–Al solid solution were observed by a transmission electron microscope, and the stacking fault energy (SFE) was determined. The specimens were annealed at …

Transactions of the Japan Institute of Metals 15(1), 39-45, 1974

J-STAGE