比内 正勝, 沢谷 昭八, 増本 量 日本金属学会誌 55 (5), 601-604, 1991
The logarithmic decrement δ and the rigidity modulus <I>G</I> were investigated for heat-treated and cold-worked Al-Ge alloys containing 2 to 20 mass%Ge. The δ and <I>G</I> values were measured by …
DOI Web Site Web Site 被引用文献1件
比内 正勝, 沢谷 昭八, 増本 量 日本金属学会誌 55 (6), 715-719, 1991
Ageing at room temperature in the logarithmic decrement δ and crystal structure were investigated for heat-treated and cold-worked Al-Zn alloys. The volue of δ was measured by an inverted pendulum …
DOI Web Site Web Site
比内 正勝, 沢谷 昭八, 増本 量 日本金属学会誌 55 (12), 1410-1414, 1991
The effects of Nb and Si on the internal friction, coercive force, and mechanical properties of Ni-25 mass%Co-Nb-Si alloys have been investigated when either furnace-cooled or water-quenched after …
中山 孝文, 菊地 紀雄, 増本 量 日本金属学会誌 53 (1), 143-148, 1989
The thermal expansion and magnetization of Mn-22%Ge based ternary alloys containing a element such as Cd or In which belongs to B group in the periodic table were measured in the air-quenching or …
比内 正勝, 沢谷 昭八, 増本 量 日本金属学会誌 53 (2), 227-231, 1989
The effect of cold working on the logarithmic decrement δ and the mechanical properties were investigated for Al-Co alloys containing 0.2 to 10.0%Co. δ and the rigidity modulus <I>G</I> were …
中村 直司, 増本 量 日本金属学会誌 51 (12), 1201-1208, 1987
The gage characteristics such as the strain gage factor <I>G</I><SUB>f</SUB>, the electrical resistivity ρ, the temperature coefficient <I>C</I><SUB>f</SUB> and the thermo-electromotive force …
比内 正勝, 沢谷 昭八, 増本 量 日本金属学会誌 51 (11), 1093-1099, 1987
The internal friction <I>Q</I><SUP>−1</SUP>, and magnetic and mecanical properties were investigated as a function of Cr concentration in Ni-Co-Nb-Cr alloys containing 25, 45 or 65%Co and 3 or 5%Nb …
中村 直司, 増本 量 日本金属学会誌 51 (5), 472-478, 1987
Investigation has been made into the electrical resistivity ρ<SUB>T</SUB> and its mean temperature coefficient <I>C</I><SUB>f</SUB> at temperatures from 293 to 373 K, the electrical resistance at …
増本 量, 比内 正勝, 沢谷 昭八 日本金属学会誌 51 (6), 584-590, 1987
The damping capacity, magnetic and mechanical properties and corrosion resistance have been investigated in Fe-Co-Mo-Cr alloys. The internal friction and magnetic hysteresis measurements, and the …
比内 正勝, 沢谷 昭八, 増本 量 日本金属学会誌 50 (6), 590-593, 1986
The influence of cold working on the damping capacity and the mechanical properties was investigated for Al-Ni alloys containing 0.2 to 12%Ni. The logarithmic decrement δ and the rigidity modulus …
DOI Web Site Web Site 被引用文献3件
村上 雄悦, 増本 量 日本金属学会誌 50 (9), 858-865, 1986
The magnetic property, electrical resistivity and hardness were measured on Ni-Fe-Cu-V alloys consisting of 60-90%Ni, 5-25%Fe, 3-30%Cu and 0.5-10%V, Ni-Fe-Cu-Nb alloys consisting of 55-85%Ni, …
増本 量, 村上 雄悦 日本金属学会誌 49 (12), 1120-1124, 1985
Magnetic property, electrical resistivity and hardness were measured on Ni-Fe-Nb-Ta alloys containing 70.50-90.12%Ni, 5.03-19.76%Fe, 0.50-10.58%Nb and 0.52-20.50%Ta. These alloys were first heated …
菊地 紀雄, 増本 量, 中山 孝文 日本金属学会誌 49 (12), 1113-1119, 1985
Young’s modulus, the thermal expansion and the magnetization in the temperature range of 120-670 K and the crystal structures at room-temperature were investigated for Mn-Ge base ternary alloys …
菊地 紀雄, 増本 量, 中山 孝文 日本金属学会誌 49 (8), 684-689, 1985
Magnetization, Young’s modulus and thermal expansion at 150-600 K and crystal structures at room temperature were investigated for Mn-Ge based ternary alloys containing Ti, V or Cr less than 14% …
中山 孝文, 増本 量, 菊地 紀雄 日本金属学会誌 49 (7), 558-561, 1985
The magnetization, the linear thermal expansion and the hardness of Mn-Sn alloys cooled down to room temperature in a furnace after homogenizing at 1070 K for 10.8 ks were investigated. …
中山 孝文, 増本 量, 菊地 紀雄 日本金属学会誌 49 (1), 84-88, 1985
The thermal expansion, magnetic property, hardness and workability were investigated for Mn-22%Ge based ternary ε phase alloys containing noble metals in the groups VII A, VIII and I B in the …
増本 量, 比内 正勝, 沢谷 昭八 日本金属学会誌 48 (3), 319-323, 1984
The logarithmic decrement δ, the rigidity modulus <I>G</I> and the tensile strength σ<SUB>t</SUB> were studied on Al-Si alloys containing 0-15%Si after heat-treating or subsequent cold-working. …
DOI Web Site 被引用文献3件
比内 正勝, 増本 量, 沢谷 昭八 日本金属学会誌 48 (3), 323-326, 1984
The influence of cold-working on the damping capacity and the mechanical properties was investigated for Al-0.2∼6 mass%Fe alloys. The logarithmic decrement δ and the rigidity modulus <I>G</I> were …
渡辺 清, 増本 量 日本金属学会誌 48 (9), 930-935, 1984
Present authors have previously reported on the permanent magnet properties of iron-rich Fe-Pt alloys and a new Platiron magnet alloy (Fe-38.5 at%Pt) with a high energy product of 159 …
DOI Web Site Web Site 被引用文献5件
増本 量, 中山 孝文, 菊地 紀雄 日本金属学会誌 48 (4), 442-447, 1984
The magnetic properties, thermal expansion, lattice constants, hardness and workability of Mn-22%Ge based ε phase ternary alloys containing transition metal in group IV, V or VI of the periodic …
比内 正勝, 増本 量, 沢谷 昭八 日本金属学会誌 48 (3), 314-319, 1984
The internal friction <I>Q</I><SUP>−1</SUP>, the magnetic hysteresis loop and the mechanical properties were investigated for three Ni-Co-Nb alloy series containing 25, 45 and 65%Co, respectively. …
増本 量, 中村 直司 日本金属学会誌 47 (10), 879-884, 1983
Measurements of the strain gage factor <I>G</I><SUB>f</SUB>, the electrical resistivity ρ at temperatures from 293 to 1273 K, the temperature coefficient of electrical resistivity …
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 47 (5), 439-445, 1983
The damping capacity and the anodic polarization behaviour in a 3%NaCl solution were studied on Fe-Mo-Cr alloys containing 1-16%Mo and 2-35%Cr after various heat-treatment. Measurement of the …
DOI Web Site Web Site 被引用文献6件
増本 量, 菊地 紀雄, 中山 孝文 日本金属学会誌 47 (6), 510-515, 1983
Young’s modulus, thermal expansion and magnetization at 120-700 K and crystal structure at room temperature were investigated for annealed Mn-Ge-Fe alloys with various crystal structures such as …
DOI Web Site Web Site 被引用文献2件
渡辺 清, 増本 量 日本金属学会誌 47 (8), 699-703, 1983
The relations between permanent magnetic properties and microstructures of Fe-34-67.5 at%Pt binary alloys were investigated using a recording fluxmeter, X-ray diffraction and electron microscopy. …
DOI Web Site Web Site 被引用文献10件
増本 量, 菊地 紀雄, 中山 孝文 日本金属学会誌 46 (10), 999-1004, 1982
The thermal expansion, magnetic properties, lattice constants, hardness and workability were measured for Mn-Ge based ternary alloys cooled at various rates after homogenizing at 1100 K for 10.8 …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 46 (4), 407-412, 1982
Measurements of Young’s modulus at 150-700 K, and thermal expansion, hardness and tensile strength at room temperature were carried out for Mn-Cu-Ti and Mn-Cu-Zr alloys subjected to various heat …
増本 量, 比内 正勝, 沢谷 昭八 日本金属学会誌 46 (9), 929-934, 1982
Effect of cold-working on the damping of furnace-cooled or water-quenched Al-Zn alloys with 0-100%Zn was studied by varying the reduction in area. Measurements of the logarithmic decrement δ and the …
林 健剛, 石井 邦彦, 伊丹 豊一 日本草地学会誌 28 (1), 96-103, 1982
...3)1年次の放牧期間中の1日増本量はTDNおよびDCP摂取量と関連が深く,重相関係数は0.761(P<0.01),寄与率58.0%であった。4)初回授精月齢はH・H区16.0,L・H区16.6,L・L区18.6か月齢で,受胎月齢はH・H,L・HおよびL・L区,それぞれ17.4,17.8,21.2か月齢であった。...
DOI Web Site
増本 量, 菊地 紀雄, 中山 孝文 日本金属学会誌 46 (3), 291-296, 1982
The thermal expansion, magnetic properties, electrical resistivity, lattice constant and hardness of Mn-Ge alloys cooled at various rates after homogenizing at 50 K below the melting point for …
増本 量, 中山 孝文 日本金属学会誌 45 (3), 322-326, 1981
A decrease in magnetostriction and an increase in magnetization with annealing time could be observed in Fe-5.66∼11.22 mass%Al alloys annealed in a magnetic field over the temperature range 573 to …
増本 量, 渡辺 清 日本金属学会誌 45 (11), 1176-1179, 1981
Magnetic properties of Fe-Pd-Ag alloys containing 17∼47 at%Pd and 1∼30 at%Ag have been measured. The coercive force of the alloys increases with increasing silver content to 12%. The 59 at%Fe, 29 …
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 45 (11), 1145-1150, 1981
The internal friction <I>Q</I><SUP>−1</SUP>, magnetic hysteresis loop, magnetostriction λ, <I>ΔG</I> effect and mechanical properties have been measured in Ni-Co alloys containing 0–70%Co. The …
DOI Web Site Web Site 被引用文献9件
増本 量, 中村 直司, 村上 雄悦 日本金属学会誌 45 (12), 1271-1278, 1981
The magnetic properties, the thermal expansion coefficient α, the electrical resistivity ρ and the hardness <I>H</I><SUB>v</SUB> have been studied for the Fe-<about 3 mass%Nb-20 mass%Co-<10 mass%W …
増本 量, 菊地 紀雄, 中山 孝文 日本金属学会誌 45 (1), 107-108, 1981
DOI Web Site 被引用文献6件
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 45 (6), 631-636, 1981
The relations of internal friction <I>Q</I><SUP>−1</SUP> with coercive force <I>H<SUB>c</SUB></I>, hysteresis loss <I>W<SUB>h</SUB></I> and magnetostriction λ for Fe-Mo alloys were studied by …
DOI Web Site Web Site 被引用文献4件
増本 量, 高橋 実, 中山 孝文 日本金属学会誌 44 (1), 107-111, 1980
The time-variations of magnetostriction and magnetization of rod shaped single crystals of Ni-25%Co alloy were observed in an external magnetic field of 6.4 kA/m at high temperatures. The …
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 43 (6), 471-474, 1979
The internal friction <I>Q</I><SUP>−1</SUP> was measured by an inverted torsion pendulum for Fe-Cr alloys containing 0∼35%Cr. The measured frequency and the maximum shear strain amplitude …
DOI Web Site Web Site 被引用文献8件
増本 量, 渡辺 清, 三寺 正雄 日本金属学会誌 43 (5), 361-363, 1979
Measurements of rigidity modulus, thermal expansion, magnetization at 293∼573 K and hardness at room temperature have been carried out for annealed Mn-Ga alloys.<BR>The results show that …
増本 量, 村上 雄悦, 中村 直司 日本金属学会誌 43 (6), 506-513, 1979
Magnetic properties, electrical resistivity and hardness were studied on Fe-Mo alloys containing less than 14.1%Mo and Fe-W alloys containing less than 13.8%W. All the alloys used in this study were …
増本 量, 菊地 紀雄, 沢谷 昭八 日本金属学会誌 43 (1), 13-17, 1979
Young’s modulus at high temperatures, thermal expansion, rigidity modulus, hardness and tensile strength at room temperature have been measured for Mn-Ni-Ti and Mn-Ni-Zr alloys subjected to various …
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 42 (12), 1134-1137, 1978
Measurements of the internal friction <I>Q</I><SUP>−1</SUP> and mechanical properties have been carried out on open-melted Fe-W alloys containing 0∼20%W. The highest <I>Q</I><SUP>−1</SUP> value of …
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 42 (1), 47-50, 1978
Ni-Fe-Nb alloys were heated in purified H<SUB>2</SUB> gas at temperatures ranging from 750 to 1150°C for 1 h. The effects of sheet thickness and heat treatment on the magnetic properties of the …
増本 量 日本応用磁気学会誌 2 (3), 61-64, 1978
DOI
増本 量, 渡辺 清, 三寺 正雄 日本金属学会誌 42 (5), 474-479, 1978
Crystal structures and magnetic properties of Mn-21.0∼35.0 at%Ga alloys have been investigated by means of X-ray diffraction, thermal expansion and magnetic measurements. It has been found that a …
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 42 (4), 337-340, 1978
The measurements of internal friction <I>Q</I><SUP>−1</SUP> under tensile loading and mechanical properties have been carried out on open-melted Fe-Co alloys containing 5∼25%Co subjected to …
増本 量, 渡辺 清 日本金属学会誌 42 (3), 256-260, 1978
An equilibrium diagram of Co-2.92∼30.05 wt%Fe binary alloys has been investigated by means of X-ray diffraction, thermal expansion measurement and microscope observation. The result shows that the …
増本 量, 村上 雄悦, 中村 直司 日本金属学会誌 42 (3), 280-284, 1978
Magnetic properties, electrical resistivity, hardness and microstructure have been studied for the Fe-Ta alloys containing less than 7%Ta. The alloys are water-quenched from various temperatures …
増本 量, 渡辺 清, 三寺 正雄 日本金属学会誌 42 (2), 169-172, 1978
An equilibrium diagram of Mn-19.0∼31.2 at%Ga binary alloys has been investigated by means of X-ray diffraction, thermal expansion and magnetic measurements. At room temerature the alloys show a …
増本 量, 中村 直司, 村上 雄悦 日本金属学会誌 42 (10), 960-966, 1978
Magnetic properties, thermal expansion coefficient, electrical resistivity and hardness have been studied for Fe-Nb-Co alloys containing less than about 4%Nb and less than 25%Co or Fe-Ta-Co alloy …
増本 量 日本金属学会会報 16 (9), 529-529, 1977
資料形態 : テキストデータ プレーンテキスト
増本 量, 沢谷 昭八, 比内 正勝 日本金属学会誌 41 (8), 820-823, 1977
The measurements of internal friction <I>Q</I><SUP>−1</SUP> and mechanical properties have been carried out for open-melted Fe-Mo alloys containing 0∼16%Mo. The <I>Q</I><SUP>−1</SUP> values linearly …
DOI Web Site Web Site 被引用文献11件
増本 量, 村上 雄悦, 中村 直司 日本金属学会誌 41 (10), 1014-1018, 1977
Magnetic properties, electrical resistivity, hardness and microstructure have been studied on Fe-Nb alloys (Recalloy) containing less than 4%Nb. The alloys are water-quenched from various …
増本 量, 中村 直司 日本金属学会誌 41 (9), 961-964, 1977
Fe-Cr-Co alloys containing less than 30% chromium and less than 70% cobalt were heated in vacuum over the temperature range of 500∼1000°C for 1 h and then furnace-cooled after cold-drawing by about …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 41 (2), 199-202, 1977
The thermal expansion, Young’s modulus, magnetic susceptibility and electrical resistivity at −150∼500°C, and the hardness and density at room temperature have been measured with annealed Mn-Pt …
増本 量, 小林 猛郎, 中山 孝文 日本金属学会誌 40 (9), 921-924, 1976
In order to determine the stability of magnetic properties, the remanence <I>B<SUB>r</SUB></I> at high temperatures has been mainly investigated for Co-36%W and Co-26%Mo alloys subjected to heat …
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 40 (7), 686-690, 1976
Ni-Fe-Ta-W alloys were heated in hydrogen atmosphere at 1150°C for 3 hr and then cooled at various rates from a temperature above their order-disorder transformation points. The highest initial …
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 40 (2), 136-139, 1976
Ni-Fe-Nb-Mo alloys were heated in hydrogen atmosphere at 1150°C for 3 hr and then cooled at various rates from a temperature above the order-disorder transformation points. The highest initial …
増本 量, 高橋 実, 中山 孝文 秋の分科会予稿集 1976.3 (0), 176-, 1976
増本 量, 渡辺 清, 大沼 繁弘 日本金属学会誌 40 (8), 812-816, 1976
Crystal structures and magnetic properties of Ir-Mn-Sb alloys were studied through X-ray and magnetic analyses. It has been found that the intermetallic compounds of the Cl<SUB>b</SUB>-type …
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 40 (8), 817-820, 1976
Ni-Fe-Nb-W alloys were heated in hydrogen atmosphere at 1150°C for 3 hr and then cooled at vairous rates from a temperature above order-disorder transformation points. The highest values of 109000 …
増本 量, 渡辺 清 日本金属学会誌 40 (2), 133-135, 1976
Crystal structures and magnetic properties of Pt<SUB>1−<I>x</I></SUB>Au<I><SUB>x</SUB></I>MnSb compounds have been investigated with a X-ray diffractometer and a magnetic balance, …
増本 量, 渡辺 清, 稲川 幸之助 日本金属学会誌 40 (3), 240-243, 1976
The magnetic properties of Co-0∼35 at%Ir alloys of the perfect <I>hcp</I> crystal structure type were studied by use of a magnetic balance and a pendulum-type magnetometer, and the following results …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 39 (2), 130-133, 1975
Young’s modulus at low and high temperatures and thermal expansion at room temperature have been measured so as to investigate the effects of additions of aluminum and tantalum on the Elinvar …
増本 量, 渡辺 清 日本金属学会誌 39 (10), 1065-1069, 1975
Crystal structures and magnetic properties of Rh-Mn-Sb alloys have been investigated by means of X-ray diffraction and magnetic measurements. It has been found that alloys in the composition range …
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 39 (11), 1127-1131, 1975
Ni-Fe-Nb-Cr alloys were heated in hydrogen atmosphere at 1150°C for 3 hr and then cooled at rates of 0.75∼300°C/hr from a temperature above the order-disorder transformation point. The highest …
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 39 (3), 281-284, 1975
Ni-Fe-Ta-Mo alloys were heated in hydrogen atmosphere at 1150°C for 3 hr and then cooled at rates of 0.75∼1400°C/hr from a temperature above order-disorder transformation point. The highest initial …
増本 量, 渡辺 清 年会予稿集 30.3 (0), 185-, 1975
増本 量, 比内 正勝, 村上 雄悦 日本金属学会誌 39 (12), 1290-1293, 1975
Ni-Fe-Ta-Cr alloys were heated in hydrogen atmosphere at 1150°C for 3 hr and then cooled at rates of 0.75∼600°C/hr from a temperature above order-disorder transformation points. The highest values …
増本 量, 菊地 紀雄, 沢谷 昭八 日本金属学会誌 39 (2), 127-130, 1975
Young’s modulus at low and high temperatures, thermal expansion and hardness at room temperature have been measured with Mn-Cu-V alloys subjected to various heat treatments and cold working. The …
増本 量, 菊地 紀雄, 沢谷 昭八 日本金属学会誌 39 (1), 67-71, 1975
Young’s modulus at high temperatures, and thermal expansion and hardness at room temperature have been measured with Mn-Ni-V alloys subjected to various heat treatments and cold working. The Young’s …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 38 (8), 749-752, 1974
Young’s modulus, thermal expansion, magnetic susceptibility and electric resistivity at −150∼400°C, and hardness at room temperature have been measured for annealed Mn-Ge alloys. It has been found …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 38 (10), 925-928, 1974
Ni-Fe-Ta alloys were vacuum melted in hydrogen atmosphere over the temperature range 1050 to 1350°C and then cooled at various rates of 100 to 8100°C/hr from a temperature above their order-disorder …
増本 量, 村上 雄悦 日本金属学会会報 13 (9), 693-694, 1974
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 38 (3), 238-241, 1974
Magnetic properties, electrical resistivity and hardness were measured with vacuum-melted Ni-Fe-Nb alloys heated in H<SUB>2</SUB> over a temperature range 950 to 1350°C and then cooled at various …
DOI Web Site 被引用文献2件
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 37 (9), 1005-1010, 1973
Measurements of Young’s modulus at −150∼400°C and of rigidity modulus, thermal expansion and hardness at room temperature have been carried out with Mn-Ni-W and Mn-Ni-W-Mo alloys subjected to …
増本 量, 渡辺 清, 大沼 繁弘 日本金属学会誌 37 (8), 872-875, 1973
Crystal structures and magnetic properties of Pd-Mn-Te alloys have been investigated by means of X-ray diffraction and magnetic balance, respectively. It has been found that the Pd-Mn-Te alloys of …
増本 量, 中村 直司 日本金属学会誌 37 (4), 462-465, 1973
The temperature coefficient of delay time, α<I><SUB>D</SUB></I>, at 0 to 40°C and the maximum gradient of magnetostriction to magnetic field, (<I>d</I>λ⁄<I>dH</I>)<I><SUB>m</SUB></I>, at room …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 37 (3), 333-337, 1973
Measurements of Young’s modulus at −150∼400°C and of rigidity modulus, thermal expansion and hardness at room temperature have been carried out for Mn-Ni-Mo alloys in the states of cold working and …
増本 量, 渡辺 清, 金子 武次郎, 井門 秀秋 年会予稿集 27.3 (0), 34-, 1972
増本 量, 渡辺 清, 稲川 幸之助 春の分科会予稿集 1972.3 (0), 32-, 1972
増本 量, 渡辺 清, 大沼 繁弘 春の分科会予稿集 1972.3 (0), 49-, 1972
増本 量, 渡辺 清, 稲川 幸之助 春の分科会予稿集 1972.3 (0), 93-, 1972
増本 量, 菊地 紀雄, 沢谷 昭八 日本金属学会誌 36 (11), 1111-1115, 1972
Measurements of thermal expansions and Young’s moduli at −150∼500°C have been carried out for single crystal specimens, 3 mm in diameter and 120 mm long, of Co-Elinvar. At the same time the rigidity …
増本 量, 村上 雄悦, 中村 直司 日本金属学会誌 36 (3), 268-269, 1972
Crystal magnetic anisotropy constant <I>K</I><SUB>1</SUB> and saturation magnetostriction λ<I><SUB>s</SUB></I> have been measured on a single crystal disk of the (100) plane and polycrystal rods of …
増本 量, 渡辺 清 日本金属学会誌 36 (9), 827-833, 1972
Crystal structures and magnetic properties of Pt-Mn-Sn alloys have been investigated by means of X-ray and magnetic analysis. It has been found that C1 or C1<SUB>b</SUB> type compound PtMnSn exists …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (5), 492-497, 1972
Measurements of Young’s modulus at −150°∼400°C and of rigidity modulus, thermal expansion and hardness at room temperature have been carried out with Mn-Cu-Mo alloys subjected to cold working and a …
増本 量, 渡辺 清 日本金属学会誌 36 (7), 680-685, 1972
Crystal structures and magnetic properties of Rh-Mn-Sb alloys have been investigated by means of X-ray and magnetic analysis. It has been found that a C1<SUB>b</SUB> type alloy exsists near the …
DOI Web Site 被引用文献7件
増本 量, 渡辺 清, 大沼 繁弘, 後藤 隆夫 年会予稿集 27.3 (0), 39-, 1972
増本 量, 渡辺 清, 三寺 正雄 年会予稿集 27.3 (0), 38-, 1972
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (11), 1116-1120, 1972
Measurements of Young’s moduli at −150∼400°C and of rigidity moduli and hardness at room temperature have been carried out with Mn-Ni-Co alloys subjected to a various procedure of heat treatment and …
増本 量, 斎藤 英夫, 中村 直司 日本金属学会誌 36 (10), 1040-1043, 1972
The strain gauge factor <I>K</I> at room temperature, the electrical resistivity ρ at 20°C, its mean temperature coefficient <I>C<SUB>f</SUB></I> and the mean thermo-electromotive force relative to …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (2), 176-181, 1972
Measurements of Young’s modulus at −150°∼400°C and of rigidity modulus and hardness at room temperature have been carried out with Mn-Cu-Co alloys subjected to a variety of heat treatment and cold …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 36 (1), 63-65, 1972
Magnetic properties, electrical resistivity and hardness of vacuum-melted Ni-Fe-Ta alloys composed of 65.00∼83.65%Ni, 8.00∼24.70%Fe and 3.20∼23.90%Ta were measured when heated in pure hydrogen …
DOI Web Site Web Site 被引用文献7件
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (1), 57-63, 1972
Measurements of Young’s modulus at −150°∼400°C and of thermal expansion, rigidity modulus and hardness at room temperature have been carried out with Mn-Cu-Fe alloys subjected to a variety of heat …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (9), 881-885, 1972
Measurements of Young’s modulus at −150∼400°C and rigidity modulus, thermal expansion and hardness at room temperature have been carried out with Mn-Ni-Cr alloys subjected to a variety of heat …
DOI Web Site 被引用文献8件
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (9), 886-890, 1972
Measurements of Young’s modulus at −150∼400°C and rigidity modulus, thermal expansion and hardness at room temperature have been carried out with Mn-Ni-Fe alloys subjected to a various procedures of …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 36 (5), 498-503, 1972
Measurements of Young’s modulus at −150°∼400°C and of rigidity modulus, thermal expansion and hardness at room temperature have been carried out with Mn-Cu-W alloys subjected to cold working and a …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 35 (12), 1150-1155, 1971
Measurements of Young’s modulus at −150°∼400°C and of thermal expansion, rigidity modulus and hardness at room temperature have been carried out with Mn-Cu-Cr alloys subjected to a variety of heat …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 35 (12), 1143-1149, 1971
Measurements of Young’s modulus and thermal expansion at −150°∼400°C, and of rigidity modulus and hardness at room temperature have been carried out with Mn-Ni alloys subject to various …
DOI Web Site Web Site 被引用文献13件
増本 量, 渡辺 清 日本金属学会誌 35 (2), 141-145, 1971
Crystal structures and magnetic properties of Au-Mn-Sb alloys have been investigated by means of X-ray and magnetic analysis. It has been found that a new Cl<SUB>b</SUB> type intermetallic compound …
増本 量, 渡辺 清, 稲川 幸之助 年会予稿集 26.3 (0), 60-, 1971
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 35 (12), 1155-1161, 1971
Measurements of Young’s modulus at −150°∼400°C and of the thermal expansion, rigidity modulus and hardness at room temperature have been carried out with Mn-Cu-Ni alloys subjected to a variety of …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 35 (10), 985-988, 1971
Measurements of magnetic properties, electrical resistivity and hardness have been carried out for Ni-Fe-Nb alloys of 72.98∼84.67%Ni, 6.59∼24.36%Fe and 2.43∼13.90%Nb heated in pure hydrogen …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 35 (7), 723-730, 1971
Measurements of Young’s modulus and thermal expansion at −150°∼400°C and of rigidity modulus and hardness at room temperature have been carried out with Mn-Cu alloys subjected to a variety of heat …
DOI Web Site Web Site 被引用文献15件
増本 量, 渡辺 清 年会予稿集 25.4 (0), 79-, 1970
増本 量, 渡辺 清 日本金属学会誌 34 (6), 638-642, 1970
Crystal srtuctures and magnetic properties of Pt-Mn-Sb alloys have been investigated by means of X-ray and magnetic analysis. It has been found that a new C1<SUB>b</SUB> type compound PtMnSb exists …
DOI Web Site 被引用文献11件
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 34 (4), 380-384, 1970
Masumoto et al. previously discovered that alloys near the composition of Ni<SUB>3</SUB>Mn exhibit high permeability by optimum heat treatments, and named them “Nimalloy”. Subsequent studies of the …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 34 (10), 1029-1033, 1970
Masumoto et al. previously discovered that alloys near in composition to Ni<SUB>3</SUB>Mn exhibited high permeability when these alloys had an optimum degree of order, and named them Nimalloy. In …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 34 (12), 1237-1242, 1970
Since the original discovery of “Nimalloy” on the Ni-Mn alloys containing about 24%Mn or less which show high permeability when rendered into an optimum degree of order by proper heat treatment. …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 34 (12), 1242-1247, 1970
Scince the original discovery of “Nimally” on Ni-Mn alloys containing less than about 24%Mn which exhibit high permeability when subjected to an appropriate heat treatments. Much work has since been …
増本 量, 渡辺 清 日本物理学会春季分科会講演予稿集 1970.4 (0), 40-, 1970
増本 量, 菊地 紀雄 日本金属学会誌 34 (8), 850-855, 1970
Rod-form single crystals of Fe-19.43%Cr alloy 3 mm in diameter and 12 cm in length were prepared, and measurements of the thermal expansion and Young’s modulus in the temperature range −150° to …
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 34 (8), 847-850, 1970
The thermal expansion at −150°∼900°C and Young’s modulus at −150°∼700°C and the rigidity modulus at room temperature of Fe-Cr alloys containing 0∼59.10%Cr have been measured, and it has been found …
増本 量, 渡辺 清 日本金属学会誌 34 (4), 385-388, 1970
Magnetic properties of quenched β′ phase alloys in the Co-Al system have been investigated by means of magnetic measurements, X-ray diffraction and nuclear magnetic resonance. The β′ phase alloys, …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 34 (1), 40-44, 1970
Masumoto et al. previously discovered high permeability alloys near in composition to Ni<SUB>3</SUB>Mn which have an optimum degree of order, and named them “Nimalloy”. Much subsequent work has …
増本 量, 渡辺 清, 三寺 正雄 日本金属学会誌 34 (12), 1247-1252, 1970
Since the discovery of a new magnet alloy “Malcolly” having a high coercive force in the system of cobalt and aluminium, much work has been carried out so as to investigate the effects of additions …
金子 武次郎, 渡辺 清, 増本 量 秋の分科会予稿集 1969.4 (0), 60-, 1969
増本 量, 渡辺 清, 大沼 繁弘 日本物理学会年会講演予稿集 24.3 (0), 68-, 1969
増本 量, 渡辺 清 日本物理学会年会講演予稿集 24.3 (0), 69-, 1969
金子 武次郎, 渡辺 清, 増本 量 日本物理学会年会講演予稿集 24.3 (0), 70-, 1969
増本 量, 沢谷 昭八, 中村 直司 日本金属学会誌 33 (9), 1003-1006, 1969
Measurements of the linear coefficient of thermal expansion, Young’s modulus and its temperature coefficient, and density were carried out so as to investigate effects of Cr, Mo or W additions on …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 33 (9), 1007-1011, 1969
Masumoto et al. previously discovered that alloys near in composition to Ni<SUB>3</SUB>Mn exhibited a high magnetic permeability when these alloys had an optimum degree of order, and named them …
増本 量, 沢谷 昭八 日本金属学会誌 33 (12), 1414-1417, 1969
Measurements of the linear coefficient of thermal expansion, Young’s modulus and its mean temperature coefficient, and density were carried out at elevated temperatures so as to investigate the …
増本 量, 沢谷 昭八 日本金属学会誌 33 (12), 1410-1413, 1969
In previous work the present authors investigated the temperature coefficient of Young’s modulus of Pd-Au alloys, and obtained a positive temperature coefficient of +2.8×10<SUP>−5</SUP> for the …
増本 量, 沢谷 昭八, 門脇 静穂 日本金属学会誌 33 (10), 1138-1140, 1969
The linear coefficient of thermal expansion, Young’s modulus and its mean temperature coefficient, and the density have been measured so as to investigate the effect of addition of Mn, Ti or Zn on …
増本 量, 沢谷 昭八 日本金属学会誌 33 (6), 685-687, 1969
The thermal expansion and Young’s modulus of the cobalt and palladium alloys have been measured in the temperature range from 0° to 990°C with a dilatometer and by means of a vibrator-controlled …
増本 量, 沢谷 昭八 日本金属学会誌 33 (1), 121-125, 1969
Young’s modulus, rigidity modulus and thermal expansion in the palladium-gold system were measured at low and high temperatures after various heat-treatments and cold works. It has been found that …
増本 量, 渡辺 清 秋の分科会予稿集 1969.4 (0), 128-, 1969
増本 量, 渡辺 清, 大沼 繁弘 秋の分科会予稿集 1969.4 (0), 129-, 1969
増本 量, 渡辺 清 秋の分科会予稿集 1969.4 (0), 129-, 1969
増本 量, 沢谷 昭八, 菊地 紀雄 日本金属学会誌 33 (9), 999-1003, 1969
Measurements of the thermal expansion, natural frequency of vibration and magnetization of ferromagnetic cobalt-manganese alloys were carried out at various temperatures, and a new equilibrium …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 33 (2), 235-239, 1969
Masumoto et al. discovered previously that alloys near the composition to Ni<SUB>3</SUB>Mn exhibit high permeability when these alloys have an optimum degree of order. These alloys were named …
増本 量, 菊地 紀雄, 沢谷 昭八 日本金属学会誌 33 (11), 1299-1303, 1969
Temperature dependences of thermal expansion and Young’s modulus of single crystals of 63%Fe-32%Ni-5%Co alloy were measured over a temperature range −30° to 600°C. The single crystal bars with …
増本 量, 沢谷 昭八, 中村 直司 日本金属学会誌 33 (10), 1134-1137, 1969
The linear coefficient of thermal expansion, Young’s modulus and its temperature coefficient, and the density have been measured so as to investigate the effect of addition of Si, Sn or V on the …
増本 量, 小林 猛郎, 村上 雄悦 日本金属学会誌 33 (10), 1141-1145, 1969
Following the discovery of high magnetic permeability alloys “Nimalloy”, the authors have carried out a series of experiments on the effects of additions of various elements on the properties of …
増本 量, 渡辺 清 日本金属学会誌 33 (10), 1145-1149, 1969
Magnetic properties of Cu-Mn-Sb alloys containing 4.98∼59.80% of Mn and 10.03∼79.71% of Sb have been measured. It has been found that the alloys consisting of about 17∼40%Mn, 10∼54%Sb and 9∼65%Cu …
増本 量, 斎藤 英夫, 沢谷 昭八 日本金属学会誌 33 (5), 593-595, 1969
The thermal expansion coefficient and the temperature coefficient of Young’s modulus of nickel-copper alloys have been determined with a vertical dilatometer previously designed by one of the …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 33 (4), 488-492, 1969
Masumoto et al. discovered previously that alloys near the Ni<SUB>3</SUB>Mn composition exhibit high-permeability by proper heat treatment. The alloys were named “Nimalloy”. In the subsequent work …
増本 量, 斎藤 英夫, 門脇 静穂 日本金属学会誌 33 (1), 126-129, 1969
Rod-form single crystals of Pd-50%Au alloy about 2 mm in diameter and 7∼10 cm in length were prepared and the thermal expansion and Young’s modulus were measured over the temperature range −150° to …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 33 (1), 130-134, 1969
Masumoto et al. discovered in the previous work high permeability alloy “Nimalloys” in the nickel and manganese system. Much subsequent works have been carried out on the effect of various element …
増本 量, 中村 直司 日本金属学会誌 32 (7), 681-684, 1968
The strain gauge factor <I>K</I> at room temperature, the electrical resistivity ρ at 20°C and its mean temperature coefficient <I>C<SUB>f</SUB></I>, and the mean thermal electromotive force …
増本 量, 中村 直司 日本金属学会誌 32 (9), 852-855, 1968
The present investigators already measured the strain gauge factor <I>K</I> and electrical properties on the wires of Fe-Cr alloys containing less than 50% chromium, and obtained the largest value …
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 32 (9), 856-860, 1968
Kobayashi and two of the present authors discovered in the previous work high permeability alloys “Nimalloy” in the nickel and manganese system. Much subsequent work has been carried out on the …
増本 量, 斎藤 英夫, 門脇 静穂 日本金属学会誌 32 (6), 529-532, 1968
Single crystals of palladium having a long length were prepared and their thermal expansions and Young’s moduli were measured over the temperature range 0° to 600°C by a dilatometer and by means of …
増本 量, 渡辺 清 秋の分科会予稿集 1968.4 (0), 73-, 1968
増本 量, 渡辺 清 日本物理学会年会講演予稿集 23.2 (0), 23-, 1968
増本 量, 村上 雄悦, 比内 正勝 日本金属学会誌 32 (5), 444-447, 1968
Kobayashi and two of the present authors have previously discovered that nickel-manganese alloys exhibit high permeability in the concentration of less than about 24% manganese and named them …
増本 量, 斎藤 英夫, 村上 雄悦, 菊地 紀雄 日本金属学会誌 32 (6), 525-528, 1968
Single crystals of nickel having a long length were prepared and their thermal expansions and Young’s moduli were measured over the temperature range 0° to 500°C by a dilatometer and by means of a …
増本 量, 小林 猛郎, 村上 雄悦 日本金属学会誌 32 (6), 521-524, 1968
The present authors previously found that nickel-manganese alloys containing less than about 24%Mn show a high permeability by proper heat treatments and named them Nimalloy. Further, Masumoto, …
増本 量, 斎藤 英夫, 菊地 紀雄 日本金属学会誌 31 (3), 263-268, 1967
The thermal expansion in the temperature range of 0° to 800°C, Young’s modulus in the temperature range of −50° to 300°C, rigidity modulus in the temperature range of 10° to 50°C and the mechanical …
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 31 (3), 259-263, 1967
Since the discovery of a new magnet alloy “Malcolloy” having a high coercive force in the system of cobalt and aluminium, the present investigators have continued researches on the effect of …
増本 量, 小林 猛郎, 村上 雄悦 日本金属学会誌 31 (9), 1117-1121, 1967
Following the disovery of a new high magnetic permeability alloy “Nimalloy” in the system of nickel and manganese, the present authors made a study of the effect of additions of iron and vanadium on …
増本 量, 斉藤 英夫 日本時計学会誌 41 (0), 97-111, 1967
増本 量, 斎藤 英夫, 菊地 紀雄 日本金属学会誌 31 (1), 25-30, 1967
Single crystals of cobalt having long length were prepared and their thermal expansion and Young’s modulus were measured over the temperature range from −100° to 350°C by a dilatometer and by means …
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 31 (3), 254-258, 1967
Since the present investigators found a new magnet alloy “Malcolloy” of high coercivity in the system of cobalt and aluminium, they have carried out studies on the effect of additions of nickel, …
増本 量, 斎藤 英夫, 菊地 紀雄 日本金属学会誌 30 (9), 885-888, 1966
The present investigators have succeeded for the first time to prepare long bar specimens of single crystals of close packed hexagonal cobalt, about 10 cm long. And with these single crystals, the …
増本 量, 小林 猛郎, 村上 雄悦 日本金属学会誌 30 (9), 837-840, 1966
The present investigators previously found a new magnetic alloy “Nimalloy” having a high permeability in the system of nickel and manganese and then made a study of the effect of iron additions on …
DOI Web Site Web Site 被引用文献12件
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 30 (7), 645-649, 1966
The present investigators previously found a new magnet alloy “Malcolloy” having a high coercive force in the system of cobalt and aluminum and then have carried out studies on the influence of the …
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 30 (9), 832-836, 1966
The present investigators previously found a new magnet alloy “Malcolloy” having a high coercive force in the system of cobalt and aluminum and then conducted studies on the influence of the …
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 29 (3), 217-222, 1965
Three years ago, the present investigators found a new magnet alloy “Malcolloy” having a high coercive force and determined the influence of the addition of nickel on their properties, the highest …
増本 量, 小林 猛郎, 村上 雄悦 日本金属学会誌 29 (11), 1101-1105, 1965
Three years ago the present investigators studied the relation between the magnetic permeability and the order-disorder transformation (Ni<SUB>3</SUB>Mn) in the ferromagnetic Ni-Mn alloys and found …
増本 量, 小林 猛郎, 村上 雄悦 日本金属学会誌 29 (3), 228-231, 1965
The magnetic properties of ferromagnetic Ni-Mn alloys containing less than 35.56% manganese have been measured at room temperature, after cooling at various rates from 900°C, with ring-form …
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 29 (3), 222-227, 1965
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 28 (7), 390-396, 1964
The present investigators already measured the magnetic properties of cobalt-rich Co-Al alloys, and found a new magnet alloy “Malcolloy” three years ago, which has a high coercive force of 1,200 Oe. …
増本 量, 斎藤 英夫, 菅井 富 日本金属学会誌 28 (2), 96-101, 1964
The mean thermal expansion coefficient in the temperature range from 20° to 50°C, and Young’s or rigidity modulus at 20°C and their mean temperature coefficient in the range of 20° to 50°C were …
増本 量, 小林 猛郎 日本金属学会誌 27 (9), 459-460, 1963
The thermal expansion coefficient and the temperature coefficient of Young’s modulus of the iron-platinum alloys have been determined with a vertical dilatometer previously designed by the present …
増本 量, 斎藤 英夫, 小林 猛郎 日本金属学会誌 27 (6), 263-265, 1963
The density ρ, Young’s modulus <I>E</I>, the thermal expansion coefficient α, and the temperature cofficient of Young’s modulus <I>e</I> were measured with the alloys of iron and palladium cooled in …
増本 量, 小林 猛郎, 渡辺 清 日本金属学会誌 27 (11), 561-565, 1963
Magnetic properties of ferromagnetic Co-Al alloys containing 4.32∼24.90% of Al have been measured. It has been found that the alloys containing more than about 10% of Al shows high coercive forces …
増本 量 日本金属学会会報 1 (1), 45-54, 1962
増本 量, 斎藤 英夫, 菅井 富, 手塚 貞至 日本金属学会誌 25 (11), 716-720, 1961
According to the rule of the small expansibility of invar proposed previously by Dr. H. Masumoto, it was proposed that there are some invar- and elinvar-type alloys in the cobalt, iron and tungsten …
増本 量, 斉藤 英夫 日本時計学会誌 18 (0), 48-57, 1961
増本 量, 斉藤 英夫 日本時計学会誌 17 (0), 20-33, 1961
増本 量, 斎藤 英夫, 高橋 実 日本金属学会誌 24 (7), 465-469, 1960
The magnetization and magnetostriction at high temperatures in a Fe<SUB>3</SUB>Cr alloy thermally demagnetized were measured simultaneously and their time changes at constant temperatures under …
増本 量, 斉藤 英夫 日本時計学会誌 16 (0), 30-40, 1960
増本 量, 斎藤 英夫, 河野 達夫, 菅井 富 日本金属学会誌 24 (5), 308-311, 1960
The influence of addition of 10, 20 and 30 per cent of nickel on the thermal expansion in the range from 20° to 50°C, the rigidity modulus at 20°C and its temperature coefficient in the range from …
増本 量, 斎藤 英夫, 菅井 富, 河野 達夫 日本金属学会誌 24 (1), 44-46, 1960
Thermal expansion coefficient, rigidity modulus and its temperature coefficient were measured for the alloys containing 45 to 80 per cent of cobalt, less than 25 per cent of molybdenum and the rest …
増本 量, 高橋 実, 杉原 真 日本金属学会誌 23 (4), 229-232, 1959
The change of the magnetization and the magnetostriction at room temperature in Fe-Co alloys was measured after magnetic annealing and the effect of magnetic annealing was observed only in the …
増本 量, 斎藤 英夫, 高橋 実, 笹川 哲三 日本物理学会春季分科会講演予稿集 1958.1 (0), 106-, 1958
増本 量, 斎藤 英夫, 高橋 実, 笹川 哲三, 河野 達夫 日本物理学会年会講演予稿集 13.2 (0), _B-155_-, 1958
増本 量, 白川 勇記, 小熊 一 日本金属学会誌 22 (3), 117-120, 1958
The frequency vs. tem perature relation of the vibrators made of Co-elinvar alloy (Fe-Co-Cr-Ni alloy) of various compositions was observed over the temperature range from about 10° to 70°, The …
増本 量, 齋藤 英夫, 高橋 実, 笹川 哲三 日本物理学会年会講演予稿集 12.6 (0), 49-, 1957
増本 量, 高橋 実, 笹川 哲三 日本物理学会春季分科会講演予稿集 1957.3 (0), 24-, 1957
増本 量, 斎藤 英夫, 菅井 富 日本金属学会誌 21 (7), 441-443, 1957
The influence of addition of 5 per cent of copper on the thermal expansion, the rigidity modulus and its temperature coefficient of alloys of cobalt, iron and chromium has been determined. The …
増本 量, 高橋 実, 笹川 哲三 秋の分科会予稿集 1956.6 (0), 50-, 1956
増本 量, 高橋 実, 笹川 哲三 日本物理学会年会講演予稿集 11.6 (0), 50-, 1956
増本 量, 斎藤 英夫, 高橋 実 日本物理学会春季分科会講演予稿集 1955.6 (0), 34-, 1955
増本 量, 斎藤 秀夫, 高橋 実 日本物理学会年会講演予稿集 1955.3 (0), 134-, 1955
増本 量, 高橋 実 日本物理学会年会講演予稿集 9.7 (0), 46-47, 1954
増本 量, 斉藤 英夫, 高橋 実 日本物理学会年会講演予稿集 9.7 (0), 46-, 1954
増本 量, 高橋 実 日本物理学会分科会講演予稿集 1953.III (0), 45-46, 1953
増本 量, 齋藤 英夫, 篠崎 方 日本金属学会誌 17 (7), 312-314, 1953
The specific heat of 17 alloys in the range of α solid solution of iron and cobalt system has been measured. It has been found that there are 3 maximum portions on the curve of the maximum …
増本 量, 齋藤 英夫, 河野 達夫 日本金属学会誌 17 (6), 255-259, 1953
The influence of an addition of 10 percent and of 20 percent of nickel on the thermal expansion in the range of 10° to 50°, rigidity modulus at 20° and its temperature coefficient in the range of …
増本 量, 齋藤 英夫, 杉原 真 日本金属学会誌 16 (8), 417-419, 1952
The specific heat of the 10 alloys consisting of iron and chromium less than 55.57 percent was measured at high temperatures in annealed, quenched and baked states by an inverse rate curve method. …
DOI Web Site 被引用文献1件 参考文献1件
増本 量, 大友 五郎, 杉原 真 日本金属学会誌 16 (3), 133-136, 1952
When the two coils in the magnetometer method are on the same axis or in parallel, the present investigators have deduced two equations showing the relations of the equivalent distance between the …
DOI Web Site 被引用文献5件
増本 量, 齋藤 英夫 日本金属学会誌 16 (3), 125-128, 1952
The mean temperature coefficient of rigidity modulus in the temperature range of 20° to 50° of the alloys of cobalt, iron and chromium containing 50 to 90 percent of cobalt and less than 20 percent …
増本 量, 齋藤 英夫, 杉原 真 日本金属学会誌 16 (7), 359-361, 1952
The specific heat of the 7 alloys in α-solid solution range of copper and zinc system was measured in annealed and quenched states by an invers rate curve method. The specific heat-temperature …
増本 量, 齋藤 英夫, 小林 猛郎 日本金属学会誌 16 (8), 420-422, 1952
According to the rule on the small expansibility of invar, previously proposed by one of the present investigators, they expected that there would be invar and elinvar-type alloys in the system of …
増本 量, 白川 勇記, 大原 亨 日本金屬學會誌.B 15 (8), 376-382, 1951
For the purpose of improving the magnetic shunt alloys hitherto used, the magnetic properties of Fe-Ni-Cr alloys,containing 30-60% of Ni,1-18% of Cr and having no allotropic transformation,were …